The authors are grateful for the financial support from Ministry of Science and Technology.

1. Preparation of Silver Precursor Ink
<ol>
	<li>Add 1.85 g of diethanolamine (DEA) in 3.15 ml deionized water.</li>
	<li>Dissolve 0.15 g of silver nitrate in 5 ml deionized water.</li>
	<li>Mix the aqueous silver nitrate solution with DEA at a 1:1 volume ratio to have 10 ml silver precursor ink right before use.</li>
</ol>
2. Fabrication of Stretchable Conductive Thin Films
<ol>
	<li>Preparation of AgNW ink
	<ol>
		<li>Dilute 2 ml of 0.5 wt% AgNWs in isopropanol with 18 ml deionized water.</li>
		<li>Place it in ultrasonic bath for 30 sec at 25 &#176;C.</li>
	</ol>
	</li>
	<li>Fabrication of AgNW thin films by auto-spray coating
	<ol>
		<li>Cut standard microscope slides into pieces of size equal to 1&#215;2.5 cm2. Prepare 16 glass pieces of this size and clean them with ethanol-wetted lens cleaning tissue.</li>
		<li>Transfer 16 ml AgNW ink (from section 1) into the paint cup of the airbrush with a pipette. Mount the airbrush on a computer-controlled robot for spray coating.</li>
		<li>Place 8 of glass pieces in a 4&#215;2 arrangement on the stage and fix them with heat-resistant tapes. The total area of all glass substrates on the stage is 4&#215;5 cm2.</li>
		<li>Set working pressure and heating stage temperature at 3 bar and 100 &#176;C, separately.</li>
		<li>Open the robot control software. Click to select brush motion command sequence under the &#34;Command&#34; column. Type in necessary input parameters to complete the auto-spraying program as shown in Figure 1. Run the program. 
		Note: The &#34;Line Speed&#34; command makes the airbrush travel at 200 mm/sec. By the &#34;Brush Area&#34; command, the airbrush moves back and forth in the direction of the short side of the glass substrate array while the stage moves along the direction of the long side and the space between two strokes is 5 mm. The &#34;Line Start&#34; and &#34;Line End&#34; commands determine the positions of starting and end points of the auto-spraying operation. The positions of them depend on the position of the glass substrate array on the stage. The &#34;Wait Point&#34; command sets a waiting time of 20 sec in the end of each auto-spraying cycle. &#34;Loop Address&#34; command enables multiple spray cycles and the number of auto-spraying cycles is 15 times. More detailed instruction of the commands can be found in the manufacturer&#39;s protocol.</li>
		<li>Change the number of auto-spraying cycles into 30 times. Repeat steps 2.2.3 - 2.2.5 to fabricate AgNW thin films of 30 spraying cycles.</li>
		<li>After spray coating, bake silver nanowire thin films on a hot plate at 120 &#176;C for 10 min.</li>
	</ol>
	</li>
	<li>&#160;Chemical soldering process
	<ol>
		<li>Cast 400 &#956;l of silver precursor ink over each spray-coated silver nanowire thin film on the glass substrate.</li>
		<li>Bake the films on a hot plate at 100 &#176;C for 40 min.</li>
		<li>Rinse the reactive coatings carefully with deionized water to remove unreactive chemical residues and air-dry the coated films.</li>
	</ol>
	</li>
	<li>Cast-peeling process
	<ol>
		<li>&#160;Cast 200 &#956;l commercially available water-based PU emulsion over each silver nano-composite thin film on the glass substrate.</li>
		<li>Air-dry the films for 10 hr to ensure full solidification.</li>
		<li>Peel off the samples from the glass substrates as free standing composite films.</li>
	</ol>
	</li>
</ol>
3. Characterization
<ol>
	<li>&#160;Stretching test
	<ol>
		<li>Turn on the linear motorized stage and wait 10 min for the machine to warm up.</li>
		<li>Open the stage control software. Set the number of the moving steps of the motor as 8,000. Click &#34;X+&#34; in the stage control software to move the mobile stage until it touches the fixed stage and click &#34;SET 0&#34; to set the position of the mobile stage as zero in the stage control software. 
		Note: The mobile stage moves 0.00125 mm in one step of the motor. For example, the mobile stage moves 1 cm if the motor moves 8,000 steps. The plus sign of &#34;X+&#34; means that the mobile stage moves in the direction of approaching fixed stage while the negative sign of &#34;X-&#34; means moving away from the fixed stage.</li>
		<li>Click &#34;X-&#34; to move the mobile stage to leave 1 cm space between the mobile and fixed stage. Secure both ends of the sample with wired holders onto the stages. Thereby, the stretching area of the sample is 1&#215;1 cm2. The setup of stretching machine is shown in Figure 2.</li>
		<li>Use the alligator clips, which are the other ends of the wiring cables to the stage holders (Figure 2), to connect to the digital multimeter for resistance measurements.</li>
		<li>Set the number of the moving steps of the motor as 800. Click &#34;X-&#34; to move the mobile stage 1 mm (10% strain) away from the fixed stage to stretch the sample and record the resistance. Repeat this step until the resistance increases significantly (~150% strain).</li>
	</ol>
	</li>
	<li>Stability test
	<ol>
		<li>Prepare the test as in steps 3.1.2 - 3.1.4.</li>
		<li>Open the digital multimeter software. Connect the digital multimeter to the computer. Long press the &#34;REL &#916;&#34; button on the digital multimeter until a computer icon appears in the upper left corner of the digital multimeter monitor. Click &#34;USB connection&#34; in the digital multimeter software and the software starts to record measured resistances.</li>
		<li>Enter commands into the input fields in the program panel of the stage control software as shown in Figure 3. The command &#34;:U-4000&#34; means to move the mobile stage 4,000 steps away from the fixed stage while the command &#34;:U4000&#34; means to move the mobile stage 4,000 steps back to the fixed stage (4,000 for 50% strain, 8,000 for 100% strain). The number of stretching cycles is 15 times. The default speed of the mobile stage is 1 mm/sec.</li>
		<li>Click &#34;Run 123&#34; in the program panel of the stage control software to execute the automatic program. The mobile stage moves in a reciprocating motion to stretch the sample with elongation cycles of triangular waveform.</li>
		<li>Click the save icon in the multimeter software and export the data of the resistance response profiles as an .xls file.</li>
	</ol>
	</li>
	<li>LED lighting test
	<ol>
		<li>Prepare the test as in steps 3.1.2 - 3.1.3. Connect the wired holders in series with a LED and a power supply.</li>
		<li>Turn on the power supply. Increase the voltage to 9 V to light the LED.</li>
		<li>Click &#34;X-&#34; to move the mobile stage 1 mm (10% strain) away from the fixed stage to stretch the sample and take a picture to record the brightness of the LED. Repeat this step until the light of LED becomes dim. Be careful that the auto-exposure of the camera should be turned off while taking pictures.</li>
	</ol>
	</li>
</ol>

<ol>
	<li>Rogers, J. A., Someya, T., Huang, Y. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Materials+and+mechanics+for+stretchable+electronics.">Materials and mechanics for stretchable electronics.</a> Science. 327 (5973), 1603-1607 (2010).</li><li>Mazzeo, A. D., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Paper-based,+capacitive+touch+pads.">Paper-based, capacitive touch pads.</a> Adv. Mater. 24 (21), 2850-2856 (2012).</li><li>Yang, C., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Silver+nanowires:+from+scalable+synthesis+to+recyclable+foldable+electronics.">Silver nanowires: from scalable synthesis to recyclable foldable electronics.</a> Adv. Mater. 23 (27), 3052-3056 (2011).</li><li>Sekitani, T., Someya, T. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Stretchable,+Large-area+Organic+Electronics.">Stretchable, Large-area Organic Electronics.</a> Adv. Mater. 22 (20), 2228-2246 (2010).</li><li>Lipomi, D. J., Tee, B. C., Vosgueritchian, M., Bao, Z. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Stretchable+organic+solar+cells.">Stretchable organic solar cells.</a> Adv. Mater. 23 (15), 1771-1775 (2011).</li><li>Liang, J., Li, L., Niu, X., Yu, Z., Pei, Q. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Elastomeric+polymer+light-emitting+devices+and+displays.">Elastomeric polymer light-emitting devices and displays.</a> Nat. Photonics. 7 (10), 817-824 (2013).</li><li>White, M. S., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Ultrathin,+highly+flexible+and+stretchable+PLEDs.">Ultrathin, highly flexible and stretchable PLEDs.</a> Nat. Photonics. 7 (10), 811-816 (2013).</li><li>Chang, I., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Performance+enhancement+in+bendable+fuel+cell+using+highly+conductive+Ag+nanowires.">Performance enhancement in bendable fuel cell using highly conductive Ag nanowires.</a> Int. J. Hydrogen Energ. 39 (14), 7422-7427 (2014).</li><li>Yan, C. Y., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=An+Intrinsically+Stretchable+Nanowire+Photodetector+with+a+Fully+Embedded+Structure.">An Intrinsically Stretchable Nanowire Photodetector with a Fully Embedded Structure.</a> Adv. Mater. 26 (6), 943-950 (2014).</li><li>Lee, M. S., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=High-performance,+transparent,+and+stretchable+electrodes+using+graphene-metal+nanowire+hybrid+structures.">High-performance, transparent, and stretchable electrodes using graphene-metal nanowire hybrid structures.</a> Nano Lett. 13 (6), 2814-2821 (2013).</li><li>Xu, F., Zhu, Y. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Highly+conductive+and+stretchable+silver+nanowire+conductors.">Highly conductive and stretchable silver nanowire conductors.</a> Adv. Mater. 24 (37), 5117-5122 (2012).</li><li>Yun, S., Niu, X., Yu, Z., Hu, W., Brochu, P., Pei, Q. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Compliant+silver+nanowire-polymer+composite+electrodes+for+bistable+large+strain+actuation.">Compliant silver nanowire-polymer composite electrodes for bistable large strain actuation.</a> Adv. Mater. 24 (10), 1321-1327 (2012).</li><li>Lee, P., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Highly+stretchable+and+highly+conductive+metal+electrode+by+very+long+metal+nanowire+percolation+network.">Highly stretchable and highly conductive metal electrode by very long metal nanowire percolation network.</a> Adv. Mater. 24 (25), 3326-3332 (2012).</li><li>Akter, T., Kim, W. S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Reversibly+Stretchable+Transparent+Conductive+Coatings+of+Spray-Deposited+Silver+Nanowires.">Reversibly Stretchable Transparent Conductive Coatings of Spray-Deposited Silver Nanowires.</a> ACS Appl. Mater. Interfaces. 4 (4), 1855-1859 (2012).</li><li>Madaria, A., Kumar, A., Ishikawa, F., Zhou, C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Uniform,+highly+conductive,+and+patterned+transparent+films+of+a+percolating+silver+nanowire+network+on+rigid+and+flexible+substrates+using+a+dry+transfer+technique.">Uniform, highly conductive, and patterned transparent films of a percolating silver nanowire network on rigid and flexible substrates using a dry transfer technique.</a> Nano Res. 3 (8), 564-573 (2010).</li><li>Lee, J., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Room-Temperature+Nanosoldering+of+a+Very+Long+Metal+Nanowire+Network+by+Conducting-Polymer-Assisted+Joining+for+a+Flexible+Touch-Panel+Application.">Room-Temperature Nanosoldering of a Very Long Metal Nanowire Network by Conducting-Polymer-Assisted Joining for a Flexible Touch-Panel Application.</a> Adv. Funct. Mater. 23 (34), 4171-4176 (2013).</li><li>Tokuno, T., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Fabrication+of+silver+nanowire+transparent+electrodes+at+room+temperature.">Fabrication of silver nanowire transparent electrodes at room temperature.</a> Nano Res. 4 (12), 1215-1222 (2011).</li><li>Garnett, E. C., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Self-limited+plasmonic+welding+of+silver+nanowire+junctions.">Self-limited plasmonic welding of silver nanowire junctions.</a> Nat. Mater. 11 (3), 241-249 (2012).</li><li>Zhu, S., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Transferable+self-welding+silver+nanowire+network+as+high+performance+transparent+flexible+electrode.">Transferable self-welding silver nanowire network as high performance transparent flexible electrode.</a> Nanotechnology. 24 (10), 1321-1327 (2013).</li><li>Han, S., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Fast+Plasmonic+Laser+Nanowelding+for+a+Cu-Nanowire+Percolation+Network+for+Flexible+Transparent+Conductors+and+Stretchable+Electronics.">Fast Plasmonic Laser Nanowelding for a Cu-Nanowire Percolation Network for Flexible Transparent Conductors and Stretchable Electronics.</a> Adv. Mater. 26 (33), 5808-5814 (2014).</li><li>Chen, S. P., Liao, Y. C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Highly+stretchable+and+conductive+silver+nanowire+thin+films+formed+by+soldering+nanomesh+junctions.">Highly stretchable and conductive silver nanowire thin films formed by soldering nanomesh junctions.</a> Phys. Chem. Chem. Phys. 16 (37), 19856-19860 (2014).</li><li>Chen, S. P., Kao, Z. K., Lin, J. L., Liao, Y. C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Silver+conductive+features+on+flexible+substrates+from+a+thermally+accelerated+chain+reaction+at+low+sintering+temperatures.">Silver conductive features on flexible substrates from a thermally accelerated chain reaction at low sintering temperatures.</a> ACS Appl. Mater. Interfaces. 4 (12), 7064-7068 (2012).</li></ol>

The authors have nothing to disclose.

The chemical soldering process can help reinforce the contact between silver nanowires. As shown in Figure 4b, the wire/wire junctions are covered with silver after applying the reactive silver ink over the spray coated AgNW thin film. The silver recovery relies strongly on the formaldehyde generated from DEA degradation, and thus the soldering process or silver reduction can be accelerated with increasing temperature.22 Because the metal surfaces of AgNWs provide effective electron exchange s...

Deformable electronic devices with large stretchability have been identified as critical parts to the realization of wearable and portable electronics in the next generation.1 Those stretchable electronic devices not only show great flexibility as those electronic devices on plastic sheets,2, 3 but also exhibit excellent performance under severe stretching or twisting conditions.4 To realize the stretchable electronics, materials with great electric performance under large deformation is needed. Recent advancements in material sciences have shown the possibility to synthesize such functional materials and have used them to design stretchable optoelectronic devices 5-9 with great tolerance to complex shape deformations. Among all the electronic functional materials, stretchable conductors are necessary to supply electrical power to those optoelectronic devices and thus are of critical importance for device performance. Because regular conducting materials, like metal or indium tin oxide, lack of mechanical robustness under large deformation, interconnects made of these materials are unable to exhibit good electrical conductivity under stretching process. Thus, elastic substrates covered with a thin layer of flexible conductive materials, such as carbon nanotube,1 graphene,10 or AgNWs,11-14 are designed for conductors with excellent stretchability. Because of the high bulk conductivity, AgNW thin films have been shown to be the most promising material for composite stretchable conductors.13 The percolating networks of AgNW thin films can effectively accommodate large elastic deformations in stretching process with great electrical conductance, and are considered as a promising stretchable electrode candidate. To implement AgNW thin films as stretchable conductors, it is necessary to have effective electrical contacts between AgNWs. After liquid deposition and drying on substrate surfaces, AgNWs regularly stack together to form a percolating mesh with loose contact points, which yield in large electrical resistances. Thus, one needs to anneal the contacts between nanowires by high-temperature or high-pressure annealing methods15-20 to reduce the contact resistances.
In contrast to these annealing processes in the literature, here, we will demonstrate a simple chemical method to anneal AgNW network connections under regular laboratory conditions.21 The fabrication process is shown in Figure 4A. A reactive ink is used to sinter the spray coated AgNW thin films on a glass plate. After reaction, the contacts between nanowires are covered with silver and hence the AgNW network is soldered chemically together. A cast-and-peel method is then used to transfer the soldered AgNW network to a stretchable PU substrate to form a composite conductor, which can exhibit no obvious change in electrical conductivity even at large tensile strain of 120%.

<table><tbody><tr><td>Silver nanowire</td><td>Sigma-Aldrich</td><td>778095-25ML</td><td>AgNW, 120 nm in diameter and 20-50 mm in length, 0.5 wt% in IPA</td></tr><tr><td>Silver nitrate crystal</td><td>Macron Fine Chemicals</td><td>MK216903</td><td></td></tr><tr><td>Diethanolamine</td><td>Sigma-Aldrich</td><td>D8885-500G</td><td></td></tr><tr><td>Polyurethane emulsion</td><td>First Chemical</td><td>20130326036</td><td>35 wt% water-based anionic polyester-polyurethane emulsion</td></tr><tr><td>Airbrush</td><td>Taiwan Airbrush &amp;amp; Equipment</td><td>AFC-sensor&amp;nbsp;</td><td></td></tr><tr><td>Desktop robot</td><td>Dispenser Tech</td><td>DT-200&amp;nbsp;</td><td></td></tr><tr><td>Digital dispenser controller</td><td>Dispenser Tech</td><td>9000E&amp;nbsp;</td><td></td></tr><tr><td>Auto-spraying program</td><td>Dispenser Tech</td><td>Smart robot edit version 3.0.0.5</td><td></td></tr><tr><td>Air compressor&amp;nbsp;</td><td>PUMA Industrial</td><td>NCS-10&amp;nbsp;</td><td></td></tr><tr><td>Linear motorized stage</td><td>TANLIAN E-O</td><td>Customized</td><td></td></tr><tr><td>Stage control software</td><td>TANLIAN E-O</td><td>Customized</td><td></td></tr><tr><td>Digital multimeter</td><td>HILA INTERNATIONAL</td><td>DM-2690TU</td><td></td></tr><tr><td>Digital multimeter software</td><td>HILA INTERNATIONAL</td><td>NA</td><td></td></tr><tr><td>Power supply</td><td>CHERN TAIH</td><td>CT-605</td><td></td></tr><tr><td>LED</td><td>PChome</td><td>M08330766</td><td>http://www.pcstore.com.tw/sun-flower/M08330766.htm</td></tr></tbody></table>

a fabrication method for highly stretchable conductors with silver nanowires

Stretchable electronics are identified as a key technology for electronic applications in the next generation. One of the challenges in fabrication of stretchable electronic devices is the preparation of stretchable conductors with great mechanical stability. In this study, we developed a simple fabrication method to chemically solder the contact points between silver nanowire (AgNW) networks. AgNW nanomesh was first deposited on a glass slide via spray coating method. A reactive ink composed of silver nanoparticle (AgNPs) precursors was applied over the spray coated AgNW thin films. After heating for 40 min, AgNPs were preferentially generated over the nanowire junctions to solder the AgNW nanomesh, and reinforced the conducting network. The chemically modified AgNW thin film was then transferred to polyurethane (PU) substrates by casting method. The soldered AgNW thin films on PU exhibited no obvious change in electrical conductivity under stretching or rolling process with elongation strains up to 120%.

The morphology of the AgNW thin film after chemical soldering process is shown in Figure 4B. Recovered AgNPs preferentially grow on the surface of AgNWs and wrap over the wire/wire junctions. Figure 5 shows the variation in sheet resistance with applied elongation strains for the unsoldered and the soldered thin films containing different amount of AgNWs. After the chemical soldering process, AgNW thin film conductors can maintain high conductivity under ...

Watch this Scientific Journal Video about A Fabrication Method for Highly Stretchable Conductors with Silver Nanowires at JoVE.com

A Fabrication Method for Highly Stretchable Conductors with Silver Nanowires

A simple synthesis method is used to chemically solder silver nanowire thin film to fabricate highly stretchable and conductive metal conductors.

Stretchable electronics are identified as a key technology for electronic applications in the next generation. One of the challenges in fabrication of ...

a-fabrication-method-for-highly-stretchable-conductors-with-silver

Universidad de Cartagena UDEC

Research

Education

JoVE Journal

JoVE Core

Engineering

Physics

Unit 1

Gauss's Law

Equilibrium and Elasticity

SCIENTISTS IN ACTION

9.8K 조회수.  National Taiwan University. A simple synthesis method is used to chemically solder silver nanowire thin film to fabricate highly stretchable and conductive metal conductors.

비디오: A Fabrication Method for Highly Stretchable Conductors with Silver Nanowires

Fabricating Nanogaps by Nanoskiving

There are several methods of fabricating nanogaps with controlled spacings, but the precise control over the sub-nanometer spacing between two electrodes-and generating them in practical quantities-is still challenging. The preparation of nanogap electrodes using nanoskiving, which is a form of edge lithography, is a fast, simple and powerful technique. This method is an entirely mechanical process which does not include any photo- or electron-beam lithographic steps and does not require any special equipment or infrastructure such as clean rooms. Nanoskiving is used to fabricate electrically addressable nanogaps with control over all three dimensions; the smallest dimension of these structures is defined by the thickness of the sacrificial layer (Al or Ag) or self-assembled monolayers. These wires can be manually positioned by transporting them on drops of water and are directly electrically-addressable; no further lithography is required to connect them to an electrometer.

The fabrication of electrically addressable, high-aspect-ratio (> 1000:1) metal nanowires separated by gaps of single nanometers using either sacrificial layers of aluminum and silver or self-assembled monolayers as templates is described. These nanogap structures are fabricated without a clean room or any photo- or electron-beam lithographic processes by a form of edge lithography known as nanoskiving.

Nanoskiving으로 Nanogaps을 제조

There are several methods of fabricating nanogaps with controlled spacings, but the precise control over the sub-nanometer spacing between two ...

연구

화학

Fabricating Metamaterials Using the Fiber Drawing Method

Metamaterials are man-made composite materials, fabricated by assembling components much smaller than the wavelength at which they operate 1. They owe their electromagnetic properties to the structure of their constituents, instead of the atoms that compose them. For example, sub-wavelength metal wires can be arranged to possess an effective electric permittivity that is either positive or negative at a given frequency, in contrast to the metals themselves 2. This unprecedented control over the behaviour of light can potentially lead to a number of novel devices, such as invisibility cloaks 3, negative refractive index materials 4, and lenses that resolve objects below the diffraction limit 5. However, metamaterials operating at optical, mid-infrared and terahertz frequencies are conventionally made using nano- and micro-fabrication techniques that are expensive and produce samples that are at most a few centimetres in size 6-7. Here we present a fabrication method to produce hundreds of meters of metal wire metamaterials in fiber form, which exhibit a terahertz plasmonic response 8. We combine the stack-and-draw technique used to produce microstructured polymer optical fiber 9 with the Taylor-wire process 10, using indium wires inside polymethylmethacrylate (PMMA) tubes. PMMA is chosen because it is an easy to handle, drawable dielectric with suitable optical properties in the terahertz region; indium because it has a melting temperature of 156.6 &deg;C which is appropriate for codrawing with PMMA. We include an indium wire of 1 mm diameter and 99.99% purity in a PMMA tube with 1 mm inner diameter (ID) and 12 mm outside diameter (OD) which is sealed at one end. The tube is evacuated and drawn down to an outer diameter of 1.2 mm. The resulting fiber is then cut into smaller pieces, and stacked into a larger PMMA tube. This stack is sealed at one end and fed into a furnace while being rapidly drawn, reducing the diameter of the structure by a factor of 10, and increasing the length by a factor of 100. Such fibers possess features on the micro- and nano- scale, are inherently flexible, mass-producible, and can be woven to exhibit electromagnetic properties that are not found in nature. They represent a promising platform for a number of novel devices from terahertz to optical frequencies, such as invisible fibers, woven negative refractive index cloths, and super-resolving lenses.

Metamaterials at terahertz frequencies offer unique opportunities, but are challenging to fabricate in bulk. We adapt the fabrication procedure for microstructured polymer optical fibers to inexpensively fabricate metamaterials potentially on an industrial scale. We produce polymethylmethacrylate fibers containing ~10 &mu;m diameter indium wires separated by ~100 &mu;m, which exhibit a terahertz plasmonic response.

섬유 그리기 방법을 사용하여 제조 Metamaterials

Metamaterials are man-made composite materials, fabricated by assembling components much smaller than the wavelength at which they operate 1. They owe ...

공학

A Method to Fabricate Disconnected Silver Nanostructures in 3D

The standard nanofabrication toolkit includes techniques primarily aimed at creating 2D patterns in dielectric media. Creating metal patterns on a submicron scale requires a combination of nanofabrication tools and several material processing steps. For example, steps to create planar metal structures using ultraviolet photolithography and electron-beam lithography can include sample exposure, sample development, metal deposition, and metal liftoff. To create 3D metal structures, the sequence is repeated multiple times. The complexity and difficulty of stacking and aligning multiple layers limits practical implementations of 3D metal structuring using standard nanofabrication tools. Femtosecond-laser direct-writing has emerged as a pre-eminent technique for 3D nanofabrication.1,2 Femtosecond lasers are frequently used to create 3D patterns in polymers and glasses.3-7 However, 3D metal direct-writing remains a challenge. Here, we describe a method to fabricate silver nanostructures embedded inside a polymer matrix using a femtosecond laser centered at 800 nm. The method enables the fabrication of patterns not feasible using other techniques, such as 3D arrays of disconnected silver voxels.8 Disconnected 3D metal patterns are useful for metamaterials where unit cells are not in contact with each other,9 such as coupled metal dot10,11or coupled metal rod12,13 resonators. Potential applications include negative index metamaterials, invisibility cloaks, and perfect lenses.
In femtosecond-laser direct-writing, the laser wavelength is chosen such that photons are not linearly absorbed in the target medium. When the laser pulse duration is compressed to the femtosecond time scale and the radiation is tightly focused inside the target, the extremely high intensity induces nonlinear absorption. Multiple photons are absorbed simultaneously to cause electronic transitions that lead to material modification within the focused region. Using this approach, one can form structures in the bulk of a material rather than on its surface.
Most work on 3D direct metal writing has focused on creating self-supported metal structures.14-16 The method described here yields sub-micrometer silver structures that do not need to be self-supported because they are embedded inside a matrix. A doped polymer matrix is prepared using a mixture of silver nitrate (AgNO3), polyvinylpyrrolidone (PVP) and water (H2O). Samples are then patterned by irradiation with an 11-MHz femtosecond laser producing 50-fs pulses. During irradiation, photoreduction of silver ions is induced through nonlinear absorption, creating an aggregate of silver nanoparticles in the focal region. Using this approach we create silver patterns embedded in a doped PVP matrix. Adding 3D translation of the sample extends the patterning to three dimensions.

Femtosecond-laser direct-writing is frequently used to create three-dimensional (3D) patterns in polymers and glasses. However, patterning metals in 3D remains a challenge. We describe a method for fabricating silver nanostructures embedded inside a polymer matrix using a femtosecond laser centered at 800 nm.

3D로 연결이 끊긴 실버 Nanostructures를 조작하는 방법

The standard nanofabrication toolkit includes  techniques primarily aimed at creating 2D patterns in dielectric media. Creating  metal patterns on a ...

Planar and Three-Dimensional Printing of Conductive Inks

Printed electronics rely on low-cost, large-area fabrication routes to create flexible or multidimensional electronic, optoelectronic, and biomedical devices1-3. In this paper, we focus on one- (1D), two- (2D), and three-dimensional (3D) printing of conductive metallic inks in the form of flexible, stretchable, and spanning microelectrodes.
Direct-write assembly4,5 is a 1-to-3D printing technique that enables the fabrication of features ranging from simple lines to complex structures by the deposition of concentrated inks through fine nozzles (~0.1 - 250 &mu;m). This printing method consists of a computer-controlled 3-axis translation stage, an ink reservoir and nozzle, and 10x telescopic lens for visualization. Unlike inkjet printing, a droplet-based process, direct-write assembly involves the extrusion of ink filaments either in- or out-of-plane. The printed filaments typically conform to the nozzle size. Hence, microscale features (&lt; 1 &mu;m) can be patterned and assembled into larger arrays and multidimensional architectures.
In this paper, we first synthesize a highly concentrated silver nanoparticle ink for planar and 3D printing via direct-write assembly. Next, a standard protocol for printing microelectrodes in multidimensional motifs is demonstrated. Finally, applications of printed microelectrodes for electrically small antennas, solar cells, and light-emitting diodes are highlighted.

Planar and three-dimensional printing of conductive metallic inks is described. Our approach provides new avenues for fabricating printed electronic, optoelectronic, and biomedical devices in unusual layouts at the microscale.

전도성 잉크의 평면 및 3 차원 인쇄

Printed electronics rely on low-cost, large-area fabrication routes to create flexible or multidimensional electronic, optoelectronic, and biomedical ...

생체공학

Evaluating Plasmonic Transport in Current-carrying Silver Nanowires

Plasmonics is an emerging technology capable of simultaneously transporting a plasmonic signal and an electronic signal on the same information support1,2,3. In this context, metal nanowires are especially desirable for realizing dense routing networks4. A prerequisite to operate such shared nanowire-based platform relies on our ability to electrically contact individual metal nanowires and efficiently excite surface plasmon polaritons5 in this information support. In this article, we describe a protocol to bring electrical terminals to chemically-synthesized silver nanowires6 randomly distributed on a glass substrate7. The positions of the nanowire ends with respect to predefined landmarks are precisely located using standard optical transmission microscopy before encapsulation in an electron-sensitive resist. Trenches representing the electrode layout are subsequently designed by electron-beam lithography. Metal electrodes are then fabricated by thermally evaporating a Cr/Au layer followed by a chemical lift-off. The contacted silver nanowires are finally transferred to a leakage radiation microscope for surface plasmon excitation and characterization8,9. Surface plasmons are launched in the nanowires by focusing a near infrared laser beam on a diffraction-limited spot overlapping one nanowire extremity5,9. For sufficiently large nanowires, the surface plasmon mode leaks into the glass substrate9,10. This leakage radiation is readily detected, imaged, and analyzed in the different conjugate planes in leakage radiation microscopy9,11. The electrical terminals do not affect the plasmon propagation. However, a current-induced morphological deterioration of the nanowire drastically degrades the flow of surface plasmons. The combination of surface plasmon leakage radiation microscopy with a simultaneous analysis of the nanowire electrical transport characteristics reveals the intrinsic limitations of such plasmonic circuitry.

Silver nanowires can simultaneously transport electrons and optical information in the form of surface plasmons. A procedure is described here to realize such a shared circuitry and the limitations at propagating both information carriers are evaluated.

Plasmonics is an emerging technology capable of simultaneously transporting a plasmonic signal and an electronic signal on the same information ...

Fabrication of Anisotropic Polymeric Artificial Antigen Presenting Cells for CD8+ T Cell Activation

Artificial antigen presenting cells (aAPC) are a promising platform for immune modulation due to their potent ability to stimulate T cells. Acellular substrates offer key advantages over cell-based aAPC, including precise control of signal presentation parameters and physical properties of the aAPC surface to modulate its interactions with T cells. aAPC constructed from anisotropic particles, particularly ellipsoidal particles, have been shown to be more effective than their spherical counterparts at stimulating T cells due to increased binding and larger surface area available for T cell contact, as well as reduced nonspecific uptake and enhanced pharmacokinetic properties. Despite increased interest in anisotropic particles, even widely accepted methods of generating anisotropic particles such as thin-film stretching can be challenging to implement and use reproducibly.
To this end, we describe a protocol for the rapid, standardized fabrication of biodegradable anisotropic particle-based aAPC with tunable size, shape, and signal presentation for T cell expansion ex vivo or in vivo, along with methods to characterize their size, morphology, and surface protein content, and to assess their functionality. This approach to fabricating anisotropic aAPC is scalable and reproducible, making it ideal for generating aAPC for &#34;off-the-shelf&#34; immunotherapies.

Here, we present a protocol to quickly and reproducibly generate biologically inspired, biodegradable articifical antigen presenting cells (aAPC) with tunable size, shape, and surface protein presentation for T cell expansion ex vivo or in vivo.

이방성 고분자 인공 항 원 제시 세포 CD8 + T 세포 활성화의 제조

Artificial antigen presenting cells (aAPC) are a promising platform for immune modulation due to their potent ability to stimulate T cells. Acellular ...

환경과학

Scalable Solution-processed Fabrication Strategy for High-performance, Flexible, Transparent Electrodes with Embedded Metal Mesh

Here, the authors report the embedded metal-mesh transparent electrode (EMTE), a new transparent electrode (TE) with a metal mesh completely embedded in a polymer film. This paper also presents a low-cost, vacuum-free fabrication method for this novel TE; the approach combines lithography, electroplating, and imprint transfer (LEIT) processing. The embedded nature of the EMTEs offers many advantages, such as high surface smoothness, which is essential for organic electronic device production; superior mechanical stability during bending; favorable resistance to chemicals and moisture; and strong adhesion with plastic film. LEIT fabrication features an electroplating process for vacuum-free metal deposition and is favorable for industrial mass production. Furthermore, LEIT allows for the fabrication of metal mesh with a high aspect ratio (i.e., thickness to linewidth), significantly enhancing its electrical conductance without adversely losing optical transmittance. We demonstrate several prototypes of flexible EMTEs, with sheet resistances lower than 1 &#937;/sq and transmittances greater than 90%, resulting in very high figures of merit (FoM) &#8211; up to 1.5 x 104 &#8211; which are amongst the best values in the published literature.

This protocol describes a solution-based fabrication strategy for high-performance, flexible, transparent electrodes with fully-embedded, thick metal mesh. Flexible transparent electrodes fabricated by this process demonstrate among the highest reported performances, including ultra-low sheet resistance, high optical transmittance, mechanical stability under bending, strong substrate adhesion, surface smoothness, and environmental stability.

Here, the authors report the embedded metal-mesh transparent electrode (EMTE), a new transparent electrode (TE) with a metal mesh completely embedded in a ...

Flow-assisted Dielectrophoresis: A Low Cost Method for the Fabrication of High Performance Solution-processable Nanowire Devices

Flow-assisted dielectrophoresis (DEP) is an efficient self-assembly method for the controllable and reproducible positioning, alignment, and selection of nanowires. DEP is used for nanowire analysis, characterization, and for solution-based fabrication of semiconducting devices. The method works by applying an alternating electric field between metallic electrodes. The nanowire formulation is then dropped onto the electrodes which are on an inclined surface to create a flow of the formulation using gravity. The nanowires then align along the gradient of the electric field and in the direction of the liquid flow. The frequency of the field can be adjusted to select nanowires with superior conductivity and lower trap density. 
In this work, flow-assisted DEP is used to create nanowire field effect transistors. Flow-assisted DEP has several advantages: it allows selection of nanowire electrical properties; control of nanowire length; placement of nanowires in specific areas; control of orientation of nanowires; and control of nanowire density in the device. 
The technique can be expanded to many other applications such as gas sensors and microwave switches. The technique is efficient, quick, reproducible, and it uses a minimal amount of dilute solution making it ideal for the testing of novel nanomaterials. Wafer scale assembly of nanowire devices can also be achieved using this technique, allowing large numbers of samples for testing and large-area electronic applications.

In this paper, flow assisted dielectrophoresis is demonstrated for the self-assembly of nanowire devices. The fabrication of a silicon nanowire field effect transistor is shown as an example.

흐름 기반 Dielectrophoresis: 고성능 솔루션 처리 나노와이어 소자의 제조에 대 한 낮은 비용 방법

Flow-assisted dielectrophoresis (DEP) is an efficient self-assembly method for the controllable and reproducible positioning, alignment, and selection of ...

Fabrication of Robust Nanoscale Contact between a Silver Nanowire Electrode and CdS Buffer Layer in Cu(In,Ga)Se2 Thin-film Solar Cells

Silver nanowire transparent electrodes have been employed as window layers for Cu(In,Ga)Se2 thin-film solar cells. Bare silver nanowire electrodes normally result in very poor cell performance. Embedding or sandwiching silver nanowires using moderately conductive transparent materials, such as indium tin oxide or zinc oxide, can improve cell performance. However, the solution-processed matrix layers can cause a significant number of interfacial defects between transparent electrodes and the CdS buffer, which can eventually result in low cell performance. This manuscript describes how to fabricate robust electrical contact between a silver nanowire electrode and the underlying CdS buffer layer in a Cu(In,Ga)Se2 solar cell, enabling high cell performance using matrix-free silver nanowire transparent electrodes. The matrix-free silver nanowire electrode fabricated by our method proves that the charge-carrier collection capability of silver nanowire electrode-based cells is as good as that of standard cells with sputtered ZnO:Al/i-ZnO as long as the silver nanowires and CdS have high-quality electrical contact. The high-quality electrical contact was achieved by depositing an additional CdS layer as thin as 10 nm onto the silver nanowire surface.

Fabrication of Robust Nanoscale Contact between a Silver Nanowire Electrode and CdS Buffer Layer in CuIn,GaSe2 Thin-film Solar Cells

In this protocol, we describe the detailed experimental procedure for the fabrication of a robust nanoscale contact between a silver nanowire network and CdS buffer layer in a CIGS thin-film solar cell.

Cu(In,Ga)Se2 박막 태양전지의 실버 나노와이어 전극과 CdS 버퍼 층 간의 견고한 나노스케일 접촉 제조

Silver nanowire transparent electrodes have been employed as window layers for Cu(In,Ga)Se2 thin-film solar cells. Bare silver nanowire electrodes ...

Iron Nanowire Fabrication by Nano-Porous Anodized Aluminum and its Characterization

Magnetic nanowires possess unique properties that have attracted the interest of different fields of research, including basic physics, biomedicine, and data storage. We demonstrate a fabrication method for iron (Fe) nanowires&#160;via electrochemical deposition into anodic&#160;alumina oxide (AAO) templates. The templates are fabricated by anodization of aluminum (Al) discs, and the pore length and diameter are controlled by changing the anodizing conditions. Pores with an average diameter of around 120 nm are created using oxalic acid as the electrolyte. Using this method, cylindrical nanowires are synthesized, which are released by dissolving the alumina using a selective chemical etchant.

In this work, we describe a&#160;protocol to fabricate iron nanowires, including the formation of the porous alumina membrane that is used as the template, electrodeposition into templates using electrolyte solution, and the release of the nanowires into the solution.

나노 다공성 양극 산화 알루미늄및 그 특성화에 의한 철 나노 와이어 제조

Magnetic nanowires possess unique properties that have attracted the interest of different fields of research, including basic physics, biomedicine, and ...