M. Abdi-Jalebi thanks Nava Technology Limited for a PhD scholarship. M.I. Dar and M.Gr&#228;tzel thank the King Abdulaziz City for Science and Technology (KACST) and the Swiss National Science Foundation (SNSF) for financial support. The authors would like to thank Dr. Pierre Mettraux in the Molecular and Hybrid Materials Characterization Center, EPFL for carrying out the XPS measurements. A.Sadhanala gratefully acknowledges financial support from the Indo-UK APEX project. S.P. Senanayak acknowledges the Royal Society London for the Newton Fellowship. R.H. Friend, M. Abdi-Jalebi, and A. Sadhanala would like to acknowledge the support from the EPSRC.

1. Synthesis and Deposition of Pristine and Additive-based CH3NH3PbI3
NOTE: All the solutions were prepared inside an argon glove box under moisture- and oxygen-controlled conditions (H2O level: &#60;1 ppm and O2 level: &#60;10 ppm).
<ol>
	<li>Dissolve 553 mg (1.2 M) of PbI2 in 1 mL of N,N-dimethylformamide (DMF) under constant stirring at 80 &#176;C.</li>
	<li>Add 0.02 M of monovalent cation halides to the PbI2 solution.</li>
	<li>Spin-coat the resulting yellow transparent solution onto the substrate (e.g., mesoporous-TiO2) for 30 s at 6,500 rpm with a ramp of 4,000 rpm.</li>
	<li>Bake the films on a hotplate at 80 &#176;C for 30 min.</li>
	<li>Dissolve 40 mg of methylammonium iodide (MAI) in 5 mL of isopropanol.</li>
	<li>Spin-coat a sufficient amount of MAI solution onto the resulting lead iodide films using a two-step protocol that includes 45 s of loading time followed by 20 s of spinning at 4,000 rpm.</li>
	<li>Anneal the spin-coated perovskite films on a hotplate at 100 &#176;C for 45 min.</li>
</ol>
2. Solar Cell Fabrication
<ol>
	<li>Substrate preparation
	<ol>
		<li>Pattern fluorine-doped tin oxide (FTO)-coated glass.
		<ol>
			<li>Cover the active area of the FTO glass with semitransparent adhesive tape.</li>
			<li>Pour the zinc (Zn) powder on the uncovered areas of the FTO substrates.</li>
			<li>Prepare 2 M of hydrochloric acid (HCl) in distilled water.</li>
			<li>Pour the HCl solution onto the part of the FTO glass that is covered with Zn powder.</li>
			<li>Wash the FTO with water and remove the tape.</li>
		</ol>
		</li>
		<li>Cleaning the substrates
		<ol>
			<li>Wash the FTO glass using 2% (w/v) detergent.</li>
			<li>Sonicate the etched FTO substrates in acetone and isopropanol (IPA) for 10 min.</li>
			<li>Treat the FTO substrates with an ultraviolet/O3 cleaner for 15 min.</li>
		</ol>
		</li>
	</ol>
	</li>
	<li>Deposition of a hole blocking layer
	<ol>
		<li>Add 0.6 mL of titanium diisopropoxide bis(acetylacetonate) (TAA) in 7 mL of IPA.</li>
		<li>Put the cleaned and patterned FTO substrates on a hotplate at 450 &#176;C and cover the contact area before heating.</li>
		<li>Spray pyrolysis the TAA solution onto the uncovered area using O2 as the carrier gas.</li>
		<li>Leave the samples at 450 &#176;C for 30 min.</li>
	</ol>
	</li>
	<li>Deposition of an electron transport layer
	<ol>
		<li>Dilute the commercial TiO2 paste (30-nm particle size) with ethanol (2:7, weight ratio).</li>
		<li>Homogenize the TiO2 dilution by sonicating for 30 min.</li>
		<li>Spin-coat the titania dilution onto the prepared samples with compact TiO2 layers for 30 s at 5,000 rpm with a ramp of 2,000 rpm.</li>
		<li>Anneal the titania films at 500 &#176;C for 30 min.</li>
		<li>Treat the resulting mesoporous TiO2 films in a 40 mM solution of TiCl4 in distilled water&#160;at 70 &#176;C for 20 min.</li>
		<li>Anneal the TiCl4-treated films at 450 &#176;C for 30 min.</li>
	</ol>
	</li>
	<li>Deposition of the perovskite layer 
	NOTE: The FTO substrates with titania layers were transferred to a dry-air box with a humidity of &#60;1% for the rest of the fabrication process.
	<ol>
		<li>Spin-coat the prepared lead iodide solutions (with and without dopants) onto the mesoporous TiO2 for 30 s at 6,500 rpm with a ramp of 4,000 rpm.</li>
		<li>Bake the films on a hotplate at 80 &#176;C for 30 min.</li>
		<li>Spin-coat a sufficient amount of MAI solution into the resulting lead iodide films using a two-step protocol that includes 45 s of loading time followed by spinning for 20 s at 4,000 rpm with a ramp of 2,000 rpm.</li>
		<li>Anneal the spin-coated perovskite films on a hotplate at 100 &#176;C for 45 min.</li>
	</ol>
	</li>
	<li>Deposition of the hole transport layer
	<ol>
		<li>Add 72.3 mg of spiro-OMeTAD to 1 mL of chlorobenzene and shake until the solution becomes transparent.</li>
		<li>Make a stock solution of bis(trifluoromethylsulphonyl)imide (LiTFSI) by adding 520 mg of LiTFSI in acetonitrile.</li>
		<li>Add 17.5 &#181;L of the LiTFSI stock solution and 28.8 &#181;L of 4-tert-butylpyridine (TBP) to the spiro-OMeTAD solution.</li>
		<li>Spin-coat the above solution for 30 s at 4,000 rpm with a ramp of 2,000 rpm.</li>
	</ol>
	</li>
	<li>Thermal evaporation of the top contact
	<ol>
		<li>Mask the samples and put them in the vacuum chamber of the evaporator.</li>
		<li>Evaporate 80 nm of gold at a rate of 0.01 nm/s.</li>
	</ol>
	</li>
</ol>

<ol>
	<li>Polman, A., Knight, M., Garnett, E. C., Ehrler, B., Sinke, W. C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Photovoltaic+materials+-+present+efficiencies+and+future+challenges.">Photovoltaic materials - present efficiencies and future challenges.</a> Science. 352, 307 (2016).</li><li>Green, M. A., Ho-Baillie, A., Snaith, H. J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=The+emergence+of+perovskite+solar+cells.">The emergence of perovskite solar cells.</a> Nat. Photonics. 8 (7), 506-514 (2014).</li><li>Stranks, S. D., Snaith, H. J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Metal-halide+perovskites+for+photovoltaic+and+light-emitting+devices.">Metal-halide perovskites for photovoltaic and light-emitting devices.</a> Nat. Nanotechnol. 10 (5), 391-402 (2015).</li><li>Snaith, H. H. J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Perovskites:+The+Emergence+of+a+New+Era+for+Low-Cost,+High-Efficiency+Solar+Cells.">Perovskites: The Emergence of a New Era for Low-Cost, High-Efficiency Solar Cells.</a> The J. Phys. Chem. Lett. 4 (21), 3623-3630 (2013).</li><li>Kojima, A., Teshima, K., Shirai, Y., Miyasaka, T. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Organometal+halide+perovskites+as+visible-light+sensitizers+for+photovoltaic+cells.">Organometal halide perovskites as visible-light sensitizers for photovoltaic cells.</a> J. Am. Chem. Soc. 131 (17), 6050-6051 (2009).</li><li>Kim, H. S., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Lead+iodide+perovskite+sensitized+all-solid-state+submicron+thin+film+mesoscopic+solar+cell+with+efficiency+exceeding+9%.">Lead iodide perovskite sensitized all-solid-state submicron thin film mesoscopic solar cell with efficiency exceeding 9%.</a> Sci. rep. 2, 591 (2012).</li><li>Jeon, N. J., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Compositional+engineering+of+perovskite+materials+for+high-performance+solar+cells.">Compositional engineering of perovskite materials for high-performance solar cells.</a> Nature. 517 (7535), 476-480 (2014).</li><li>Li, X., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=A+vacuum+flash-assisted+solution+process+for+high-efficiency+large-area+perovskite+solar+cells.">A vacuum flash-assisted solution process for high-efficiency large-area perovskite solar cells.</a> Science. 353 (6294), 58-62 (2016).</li><li>Manser, J. S., Kamat, P. V. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Band+filling+with+free+charge+carriers+in+organometal+halide+perovskites.">Band filling with free charge carriers in organometal halide perovskites.</a> Nat. Photonics. 8 (9), 737-743 (2014).</li><li>Xing, G., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Long-Range+Balanced+Electron-+and+Hole-Transport+Lengths+in+Organic-Inorganic+CH3NH3PbI3.">Long-Range Balanced Electron- and Hole-Transport Lengths in Organic-Inorganic CH3NH3PbI3.</a> Science. 342 (6156), 344-347 (2013).</li><li>Stranks, S. D., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Electron-Hole+Diffusion+Lengths+Exceeding+1+Micrometer+in+an+Organometal+Trihalide+Perovskite+Absorber.">Electron-Hole Diffusion Lengths Exceeding 1 Micrometer in an Organometal Trihalide Perovskite Absorber.</a> Science. 342 (6156), 341-344 (2013).</li><li>Pazos-Outon, L. M., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Photon+recycling+in+lead+iodide+perovskite+solar+cells.">Photon recycling in lead iodide perovskite solar cells.</a> Science. 351 (6280), 1430-1433 (2016).</li><li>Saliba, M., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Cesium-containing+Triple+Cation+Perovskite+Solar+Cells:+Improved+Stability,+Reproducibility+and+High+Efficiency.">Cesium-containing Triple Cation Perovskite Solar Cells: Improved Stability, Reproducibility and High Efficiency.</a> Energy Environ. Sci. 9 (6), (2016).</li><li>Pellet, N., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Mixed-organic-cation+perovskite+photovoltaics+for+enhanced+solar-light+harvesting.">Mixed-organic-cation perovskite photovoltaics for enhanced solar-light harvesting.</a> Angew. Chemie - Int. Ed. 53 (12), 3151-3157 (2014).</li><li>Hao, F., Stoumpos, C. C., Chang, R. P. H., Kanatzidis, M. G. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Anomalous+band+gap+behavior+in+mixed+Sn+and+Pb+perovskites+enables+broadening+of+absorption+spectrum+in+solar+cells.">Anomalous band gap behavior in mixed Sn and Pb perovskites enables broadening of absorption spectrum in solar cells.</a> J. Am. Chem. Soc. 136 (22), 8094-8099 (2014).</li><li>Dar, M. I., Abdi-Jalebi, M., Arora, N., Gr&#228;tzel, M., Nazeeruddin, M. K. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Growth+Engineering+of+CH+3+NH+3+PbI+3+Structures+for+High-Efficiency+Solar+Cells.">Growth Engineering of CH 3 NH 3 PbI 3 Structures for High-Efficiency Solar Cells.</a> Adv. Energy Mater. 6 (2), 1501358 (2016).</li><li>Ibrahim Dar, M., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Understanding+the+Impact+of+Bromide+on+the+Photovoltaic+Performance+of+CH3+NH3+PbI3+Solar+Cells.">Understanding the Impact of Bromide on the Photovoltaic Performance of CH3 NH3 PbI3 Solar Cells.</a> Adv. Mater. 27 (44), 7221-7228 (2015).</li><li>Abdi-Jalebi, M., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Impact+of+Monovalent+Cation+Halide+Additives+on+the+Structural+and+Optoelectronic+Properties+of+CH+3+NH+3+PbI+3+Perovskite.">Impact of Monovalent Cation Halide Additives on the Structural and Optoelectronic Properties of CH 3 NH 3 PbI 3 Perovskite.</a> Adv. Energy Mater. 6 (10), 1502472 (2016).</li><li>Yin, W. J., Shi, T., Yan, Y. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Unusual+defect+physics+in+CH3NH3PbI3+perovskite+solar+cell+absorber.">Unusual defect physics in CH3NH3PbI3 perovskite solar cell absorber.</a> Appl. Phys. Lett. 104 (6), 063903/1-063903/4 (2014).</li><li>Agiorgousis, M. L., Sun, Y. Y., Zeng, H., Zhang, S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Strong+Covalency-Induced+Recombination+Centers+in+Perovskite+Solar+Cell+Material+CH+3+NH+3+PbI+3.">Strong Covalency-Induced Recombination Centers in Perovskite Solar Cell Material CH 3 NH 3 PbI 3.</a> J. Am. Chem. Soc. 136 (41), 14570-14575 (2014).</li><li>Andaji Garmaroudi, Z., Abdi-Jalebi, M., Mohammadi, M. R. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=A+facile+low+temperature+route+to+deposit+TiO2+scattering+layer+for+efficient+dye-sensitized+solar+cells.">A facile low temperature route to deposit TiO2 scattering layer for efficient dye-sensitized solar cells.</a> RSC Adv. 6 (75), (2016).</li><li>Abdi-Jalebi, M., Mohammadi, M. R., Fray, D. J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Double-Layer+TiO2+Electrodes+with+Controlled+Phase+Composition+and+Morphology+for+Efficient+Light+Management+in+Dye-Sensitized+Solar+Cells.">Double-Layer TiO2 Electrodes with Controlled Phase Composition and Morphology for Efficient Light Management in Dye-Sensitized Solar Cells.</a> J. of Clust. Sci. 25 (4), 1029-1045 (2014).</li><li>Abdi-Jalebi, M., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Impact+of+a+Mesoporous+Titania-Perovskite+Interface+on+the+Performance+of+Hybrid+Organic-Inorganic+Perovskite+Solar+Cells.">Impact of a Mesoporous Titania-Perovskite Interface on the Performance of Hybrid Organic-Inorganic Perovskite Solar Cells.</a> The J. Phys. Chem. Lett. 7 (16), 3264-3269 (2016).</li></ol>

The authors declare that they have no competing financial interests.

A typical architecture of mesoscopic perovskite solar cells was used in this work, where a series of materials were spin-coated between a conductive substrate and a thermally-evaporated metal contact (Figure 1). The mesoporous TiO2 layers were treated with TiCl4, which is reported to passivate the surface traps and to improve the interface between the electron transport layer and the absorber material21,22. The perovskite layer was then deposited using a sequential two-step deposition technique. The full conversion of lead halide into perovskite in the second step is essential to achieve the highest light absorption16,17, and we showed that the monovalent cation halide additives (e.g., NaI and CuBr) result in a complete conversion. Furthermore, the complete coverage of the mesoporous titania layer with the perovskite over-layer is vital to eliminate potential recombination between the hole transport layer (e.g., Spiro OMETAD) and the electron transport layer (e.g., mesoporous TiO2)23. We illustrated that adding the monovalent cation halides (e.g., CuI and AgI) can improve the surface coverage of the perovskite capping layer, which leads to a higher open circuit voltage for the device.
The main advantage of our method is the doping step, where we incorporated monovalent cations into the CH3NH3PbI3 structure to improve the density of charges, the charge transport, and the conductivity of the absorber layer. As stated in the previous section, the aforementioned dopants significantly enhanced both the electron and the hole mobilities. In addition, a remarkable decrease in the charge transport activation energy, as well as in the energetic disorder of the perovskite film, was achieved by monovalent cation doping.
In this work, we have demonstrated a method to dope CH3NH3PbI3 as an absorber layer in the mesoscopic perovskite solar cell structure. Monovalent cation halides were used to tune the morphological, optical, and electrical properties of CH3NH3PbI3 perovskite film in order to enhance the photovoltaic performance. Therefore, we incorporated three different monovalent cations (i.e., Na+, Cu+, and Ag+), which have similar ionic radii to Pb2+, in the lead source in the sequential two-step deposition of CH3NH3PbI3. As a result, a remarkable improvement in the structural and optoelectronic properties of CH3NH3PbI3 occurred in the presence of these additives, leading to higher PCEs for the fabricated solar cells. Therefore, our work highlights a facile way of doping the CH3NH3PbI3 as an absorber layer, which can be used in all other configurations of perovskite solar cells (e.g., planar architecture) in order to further improve the electronic quality of perovskite thin films.
The data underlying this paper are available at: https://www.repository.cam.ac.uk/handle/1810/260187.

Currently, the dominant portion of the world&#39;s energy requirement (i.e., 85%) is being supplied by the combustion of oil, coal, and natural gas, which facilitates global warming and has deleterious effects on our environment1. Therefore, the development of CO2-neutral sources of energy is of paramount interest. Photovoltaics (PV) is an ideal energy conversion process that can meet this requirement. However, cost and efficiency, as the main obstacles to the extensive adoption of PV technology, must be improved. Emerging PV technologies based on new materials, such as perovskite solar cells (PSC), have the combination of lower cost and greater efficiency. This is achieved through the utilization of cheap materials that are readily available, as well as through fast, facile, and low-energy processing routes compared to silicon-based counterparts2,3,4. A remarkable improvement in the power conversion efficiency (PCE), from 3.8% to more than 22%, has been reported for hybrid organic-inorganic lead halide perovskite since its first appearance in PV architecture5,6,7,8. Such a superb performance originates from the strong light absorption with an extremely sharp band-edge, the very low energetic disorder, the weakly-bound excitons that easily dissociate into free carriers with large diffusion lengths, and the photon recycling capability of hybrid organic-inorganic lead halide perovskite9,10,11,12. These materials are categorized in the perovskite family, which are crystallized from organic halide and metal halide salts to form crystals in the ABX3 structure, where X is an anion and A and B are cations of different sizes (A being larger than B). Reported cations for the A site include methylammonium (MA), formamidinium (FA), and cesium (Cs); a combination of these cations shows the highest performance13,14. Furthermore, the main candidate for the divalent cation in the B site is lead, which can be replaced by tin; the bandgap can be successfully red-shifted to over 1,000 nm in a lead-tin mixed perovskite15. Similarly, the X-site occupants have been studied extensively, where a mixture of iodide (I) and bromide (Br) were introduced as the main candidates16,17. Therefore, it is highly plausible to manipulate the structural, morphological, and optoelectronic properties of perovskites by altering their chemical composition.
Despite the fact that the enhanced crystalline quality and the macroscopic uniformity of the perovskite film are key parameters to achieve efficient devices18, the impact of the boundaries between the polycrystalline domains, the origin and role of electronic defects in the perovskite absorbers, and the role of the charge collection layers upon loss processes in the perovskite solar cells are not yet well understood. Regarding the nature of electronic defects in the perovskite structure, it has been reported that many of the defects, such as I or Pb vacancies, result in states that are very close to or within the continuum of states in the conduction and valence bands, which might have a negative electronic impact on the photovoltaic devices19. In addition, a strong covalent bonding interaction between lead cations and iodide anions in the perovskite plane may lead to the existence of intrinsic defects (e.g., under-coordinated Pb dimers and I trimers), which could create sites within the band-edge that act as charge recombination centers during the operation of the device20.
Here, we investigate the impact of doping CH3NH3PbI3 perovskite with monovalent cation halides, including Na+, Cu+, and Ag+, lower-valence metal ions than Pb2+. We therefore incorporate these cations through the addition of a rational amount of their halide-based salts (e.g., NaI, CuBr, CuI, and AgI) into the perovskite precursor solution. These cations have ionic radii similar to Pb2+, so substitutional doping within the crystal is probable. We have shown that the presence of these cations strongly affects both the morphology and coverage of the perovskite layer. In addition, the presence of these cations (e.g., Na+ and Ag+) has been confirmed by X-ray photoelectron spectroscopy (XPS), and a significant change in the Fermi level of perovskite was measured by Kelvin probe force microscopy (KPFM). By incorporating these cations into sequentially deposited perovskite solar cells, we achieved an improvement in the photovoltaic efficiency of PSC (15.6% compare to 14%). Therefore, it is very essential to enhance the structural and optoelectronic properties of the absorber layer (e.g., perovskite) in solar cell architecture to maximize the charge transport and to passivate the surface traps in order to reach the highest PV performance.

<table><tbody><tr><td>Fluorine doped Tin Oxide (FTO)-coated glass</td><td>Sigma-Aldrich&amp;nbsp;</td><td>735264-1EA</td><td>Resistivity&amp;asymp;13 &amp;Omega;/sq</td></tr><tr><td>Zinc powder</td><td>Sigma-Aldrich&amp;nbsp;</td><td>96454</td><td>Molecular Weight 65.39&amp;nbsp;</td></tr><tr><td>Hydrochloric acid&amp;nbsp;</td><td>Sigma-Aldrich&amp;nbsp;</td><td>84415</td><td>&amp;ge;37 wt. %</td></tr><tr><td>Hellmanex detergent&amp;nbsp;</td><td>Sigma-Aldrich&amp;nbsp;</td><td>Z805939-1EA</td><td>pkg of 1 L&amp;nbsp;</td></tr><tr><td>Titanium diisopropoxide bis(acetylacetonate)&amp;nbsp;</td><td>Sigma-Aldrich&amp;nbsp;</td><td>325252</td><td>75&amp;nbsp;wt. % in isopropanol</td></tr><tr><td>Titania Paste</td><td>DYESOL</td><td>MS002300</td><td>30 NR-D Transparent Titania Paste</td></tr><tr><td>Lead(II) iodide</td><td>Sigma-Aldrich</td><td>211168</td><td>99 wt. %</td></tr><tr><td>&lt;em&gt;N,N&lt;/em&gt;-Dimethylformamide&amp;nbsp;</td><td>Sigma-Aldrich&amp;nbsp;</td><td>437573</td><td>ACS reagent, &amp;ge;99.8%</td></tr><tr><td>Methylammonium iodide</td><td>DYESOL</td><td>MS101000</td><td>Powder&amp;nbsp;</td></tr><tr><td>SpiroMeOTAD</td><td>Sigma-Aldrich&amp;nbsp;</td><td>792071</td><td>99% (HPLC)</td></tr><tr><td>Bis(trifluoromethane)sulfonimide lithium salt</td><td>Sigma-Aldrich&amp;nbsp;</td><td>544094</td><td>99.95% trace metals basis&amp;nbsp;</td></tr><tr><td>4-&lt;em&gt;tert&lt;/em&gt;-Butylpyridine</td><td>Sigma-Aldrich&amp;nbsp;</td><td>142379</td><td>Purity: 96%</td></tr><tr><td>Chlorobenzene</td><td>Sigma-Aldrich</td><td>284513</td><td>anhydrous, 99.8%</td></tr><tr><td>2-Propanol (IPA)</td><td>Sigma-Aldrich&amp;nbsp;</td><td>278475</td><td>anhydrous, 99.5%&amp;nbsp;</td></tr><tr><td>Ethanol</td><td>Sigma-Aldrich</td><td>2860</td><td>absolute alcohol, without additive, &amp;ge;99.8%</td></tr></tbody></table>

monovalent cation doping of ch3nh3pbi3 for efficient perovskite solar cells

Here, we demonstrate the incorporation of monovalent cation additives into CH3NH3PbI3 perovskite in order to adjust the optical, excitonic, and electrical properties. The possibility of doping was investigated by adding monovalent cation halides with similar ionic radii to Pb2+, including Cu+, Na+, and Ag+. A shift in the Fermi level and a remarkable decrease of sub-bandgap optical absorption, along with a lower energetic disorder in the perovskite, was achieved. An order-of-magnitude enhancement in the bulk hole mobility and a significant reduction of transport activation energy within an additive-based perovskite device was attained. The confluence of the aforementioned improved properties in the presence of these cations led to an enhancement in the photovoltaic parameters of the perovskite solar cell. An increase of 70 mV in open circuit voltage for AgI and a 2 mA/cm2 improvement in photocurrent density for NaI- and CuBr-based solar cells were achieved compared to the pristine device. Our work paves the way for further improvements in the optoelectronic quality of CH3NH3PbI3 perovskite and subsequent devices. It highlights a new avenue for investigations on the role of dopant impurities in crystallization and controls the electronic defect density in perovskite structures.

Field emission scanning electron microscopy (FESEM) was used to record both cross-sectional images of the fabricated perovskite solar cells (Figure 1) and top view images of the deposited PbI2 and CH3NH3PbI3 films (Figure 2). X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS) were employed to characterize the structural properties of the perovskite films (Figures 3 and 4). Photothermal deflection spectroscopy (PDS) and Kelvin probe force microscopy (KPFM) were used to probe the optical and electrical properties of the perovskite films, respectively (Figures 5 and 6). Furthermore, temperature-dependent bulk transport measurements based on space charge limited current (SCLC) was performed on the perovskite devices (Figure 7). Finally, a standard photovoltaic measurement of the fabricated devices was performed (Figure 8 and Table 1).
Based on the top-view SEM images of the PbI2 and CH3NH3PbI3 deposited on the mesoporous TiO2 layer (mp-TiO2) shown in Figure 2, the effect of the additives on the morphology of perovskite was illustrated where large branch-shaped crystals of PbI2 were achieved in the NaI-based sample. This led to the formation of larger asymmetric crystals of perovskite. Furthermore, we obtained a uniform and pinhole-free perovskite capping layer for CuI- and AgI-based samples (Figure 2c and 2e). To investigate the effect of monovalent cation halide additives on the crystal structure of CH3NH3PbI3 and on the conversion of PbI2 into CH3NH3PbI3, X-ray diffraction was performed (Figure 3). Although the crystal structure of the final perovskite remained the same for all samples, it is evident that the diffraction peak at 2&#952; = 12.6, which corresponds to the unconverted PbI2, was eliminated in the presence of NaI and CuBr additives. In order to confirm the presence of these monovalent cations within the CH3NH3PbI3 perovskite films, we carried out an XPS analysis, as shown in Figure 4. On the basis of the XPS data, we demonstrated the presence of Na and Ag ions within the perovskite films, whereas the concentration of Cu could not be estimated, probably due to the nearness of iodide (I 3p1/2) and copper (Cu 2p1/2) peaks.
The effect of the monovalent cation additives on the absorption spectrum of the perovskite is shown in Figure 5a, which was measured by PDS. It is evident that the additive-based CH3NH3PbI3 had lower sub-bandgap absorption compared to the pristine sample. Furthermore, an absorption tail was observed for Cu-based samples, which originated from the intrinsic absorption of copper halide (Figure 5b). Although the absorption tail confirms the presence of Cu cations in the final perovskite films, it is evident, based on the comparison between the PDS of CuI-based PbI2 and CH3NH3PbI3, that their incorporation is not complete. In addition, the Urbach energy (Eu), which is a measure of the degree of energetic disorder of a material, was estimated for pristine, NaI-, CuBr-, CuI-, and AgI-based perovskite, and the values are 15.6, 11.8, 12.8, 13.5, and 15.2 meV, respectively (inset of Figure 5a).
To explore the influence of the aforementioned additives on the electronic structure of CH3NH3PbI3, we performed KPFM, where the contact potential difference (CPD) of the line profiles was measured. This corresponds to the surface work function (&#934;) of the perovskite shown in Figure 6. A clear shift in the CPD (i.e., 0.1 V) of additive-based perovskite compared to the pristine one shows that the perovskite Fermi level is shifted towards the valence band. This change in the Fermi level of perovskite can be attributed to either substitutional p-doping (e.g., the replacement of Pb2+ with monovalent cations X+) or surface passivation at the crystalline surfaces of perovskite.
To investigate the effect of doping on the density of the charges and on their transport properties in CH3NH3PbI3, we performed temperature-dependent bulk transport measurements (Figure 7a). We then estimated the bulk carrier mobility (&#956;SCL) based on the space charge limited current (SCLC) of the complete electron and hole-only pristine and additive-based perovskite devices. A remarkable increase in the conductivity and in both the electron and hole mobilities were achieved, particularly for the NaI and CuBr samples compared to pristine perovskite (Table 1). It is notable that the improvement in the charge mobility and conductivity are consistent with the enhancement in the short circuit current (Jsc) and fill factor (FF) of the fabricated solar cells shown in Figure 7b. Furthermore, we estimated the activation energy for charge transport (EA) for both the electron and the hole using temperature-dependent bulk transport measurements, where a clear decrease was achieved for additive-based perovskite. This improvement is attributed to the higher density of carriers because of doping and filling the transport traps, which results in a significant decline in the transport barrier.
We fabricated perovskite solar cells based on the aforementioned monovalent cation halides, the corresponding J-V curves, and the photovoltaic parameters that are summarized in Figure 8a and Table 1. A significant improvement in open circuit voltage was achieved for both CuI- (0.99 V) and AgI- (1.02 V) based solar cells because of the ideal surface coverage (Figure 2c and 2e). Furthermore, a remarkable increase in the short circuit current (&#8776;2 mA cm-2) for CuBr- and NaI-based solar cells was attained, which can be ascribed to the full conversion of PbI2 into CH3NH3PbI3. This improvement was confirmed by the incident photon-to-current conversion efficiency (IPCE) spectra shown in Figure 8b. Finally, higher power conversion efficiency (PCE) levels of 15.2%, 15.6%, and 15.3% were achieved for NaI-, CuBr-, and CuI-based devices, respectively, compare to the 14.0% value for the pristine perovskite solar cell.
<img alt="Figure 1" src="/files/ftp_upload/55307/55307fig1.jpg" /> 
Figure 1: Mesoscopic perovskite solar cell architecture. SEM cross-sectional micrograph of a complete device with the following structure: FTO/compact-TiO2/mesoporous-TiO2/CH3NH3PbI3/Spiro-OMeTAD/Au.
<img alt="Figure 2" src="/files/ftp_upload/55307/55307fig2.jpg" /> 
Figure 2: Morphological analysis of lead iodide and perovskite structures. Top-view SEM images of PbI2 (left side) and CH3NH3PbI3 (right side) structures: (a) pristine, (b) CuBr-, (c) CuI-, (d) NaI-, and (e) AgI-based perovskite samples deposited on a mesoporous TiO2-coated FTO. This figure has been reproduced from reference18. <a href="http://cloudflare.jove.com/files/ftp_upload/55307/55307fig2large.jpg" target="_blank">Please click here to view a larger version of this figure.</a>
<img alt="Figure 3" src="/files/ftp_upload/55307/55307fig3.jpg" /> 
Figure 3: Effect of monovalent cation halide additives on perovskite crystallinity. X-ray diffraction spectra of pristine and additive-based CH3NH3PbI3 perovskite that is grown on mesoporous TiO2 film, which is deposited on the FTO-coated glass. This figure has been reproduced from reference18. <a href="http://cloudflare.jove.com/files/ftp_upload/55307/55307fig3large.jpg" target="_blank">Please click here to view a larger version of this figure.</a>
<img alt="Figure 4" src="/files/ftp_upload/55307/55307fig4.jpg" /> 
Figure 4: Trace of monovalent cations in the CH3NH3PbI3 perovskite structure. XPS analysis of pristine, CuBr-, CuI-, NaI-, and AgI-based perovskite films. This figure has been reproduced from reference18. <a href="http://cloudflare.jove.com/files/ftp_upload/55307/55307fig4large.jpg" target="_blank">Please click here to view a larger version of this figure.</a>
<img alt="Figure 5" src="/files/ftp_upload/55307/55307fig5.jpg" /> 
Figure 5: Optical properties of perovskite films. (a) The absorption spectra of perovskite films derived from pristine and additive-based lead sources measured using the PDS technique. The inset shows the corresponding Urbach energies for all samples. The error bar is defined by the SD in fitting the Urbach tail. (b) Comparison of the PDS absorption spectra of pristine and CuBr-based lead iodide and perovskite films, as well as CuBr deposited on ms-TiO2 and CuBr-only films. This figure has been reproduced from reference18. <a href="http://cloudflare.jove.com/files/ftp_upload/55307/55307fig5large.jpg" target="_blank">Please click here to view a larger version of this figure.</a>
<img alt="Figure 6" src="/files/ftp_upload/55307/55307fig6.jpg" /> 
Figure 6: Effect of monovalent cation additives on the surface potential of perovskite films. CPD line profiles recorded from pristine and additive-based perovskite films using KPFM. The AFM topography image is shown on the top. This figure has been reproduced from reference18. <a href="http://cloudflare.jove.com/files/ftp_upload/55307/55307fig6large.jpg" target="_blank">Please click here to view a larger version of this figure.</a>
<img alt="Figure 7" src="/files/ftp_upload/55307/55307fig7.jpg" /> 
Figure 7: Charge transport characteristics of perovskite films. (a) J-V characteristics of hole-only devices (ITO/PEDOT:PSS/Perovskite/Au), utilized for estimating the SCLC hole mobility. Note that the current density (J) is scaled with the thickness of the perovskite layers. (b) The trends in the Jsc, &#181;h, and &#181;e for pristine and additive-based perovskite. This figure has been reproduced from reference18. <a href="http://cloudflare.jove.com/files/ftp_upload/55307/55307fig7large.jpg" target="_blank">Please click here to view a larger version of this figure.</a>
<img alt="Figure 8" src="/files/ftp_upload/55307/55307fig8.jpg" /> 
Figure 8: Photovoltaic performance characteristics. (a) Current-voltage characteristics of devices under an illumination of 100 mW/cm2, obtained using different types of monovalent cation halides added to the lead source solution. (b) Incident photon-to-current efficiency (IPCE) spectra as a function of the wavelength of monochromatic light for the pristine, CuBr-, CuI-, NaI-, and AgI-based perovskite solar cells. This figure has been reproduced from reference18. <a href="http://cloudflare.jove.com/files/ftp_upload/55307/55307fig8large.jpg" target="_blank">Please click here to view a larger version of this figure.</a>
<table border="1" fo:keep-together.within-page="1" fo:keep-with-next.within-page="always">
	<tbody>
		<tr>
			<td>Type of Sample</td>
			<td>JSC</td>
			<td>VOC</td>
			<td>FF</td>
			<td>PCE</td>
			<td>&#956;e</td>
			<td>&#956;h</td>
			<td>EAe</td>
			<td>EAh</td>
		</tr>
		<tr>
			<td></td>
			<td>(mA cm-2)</td>
			<td>(V)</td>
			<td></td>
			<td>(%)</td>
			<td>(cm2/Vs)</td>
			<td>(cm2/Vs)</td>
			<td>(meV)</td>
			<td>(meV)</td>
		</tr>
		<tr>
			<td>Pristine</td>
			<td>21.03</td>
			<td>0.95</td>
			<td>0.70</td>
			<td>14.01</td>
			<td>0.02</td>
			<td>0.008</td>
			<td>135</td>
			<td>198</td>
		</tr>
		<tr>
			<td>CuBr</td>
			<td>22.92</td>
			<td>0.95</td>
			<td>0.72</td>
			<td>15.61</td>
			<td>0.05</td>
			<td>0.04</td>
			<td>88</td>
			<td>132</td>
		</tr>
		<tr>
			<td>CuI</td>
			<td>21.81</td>
			<td>0.99</td>
			<td>0.71</td>
			<td>15.25</td>
			<td>0.02</td>
			<td>0.036</td>
			<td>94</td>
			<td>157</td>
		</tr>
		<tr>
			<td>NaI</td>
			<td>22.97</td>
			<td>0.9</td>
			<td>0.73</td>
			<td>15.14</td>
			<td>0.04</td>
			<td>0.07</td>
			<td>77</td>
			<td>137</td>
		</tr>
		<tr>
			<td>AgI</td>
			<td>19.24</td>
			<td>1.02</td>
			<td>0.72</td>
			<td>14.18</td>
			<td>0.005</td>
			<td>0.006</td>
			<td>105</td>
			<td>177</td>
		</tr>
	</tbody>
</table>
Table 1: Photovoltaic and charge transport parameters of PSC. Summary of the photovoltaic parameters derived from J-V measurements and charge mobilities, along with the activation energy for the pristine and additive-based perovskite solar cells that show the best performance and were fabricated using the two-step deposition method. It is notable that the statistics of the photovoltaic parameters follow the same trend as the best performing devices. This table has been reproduced from reference18.

Watch this Scientific Journal Video about Monovalent Cation Doping of CH3NH3PbI3 for Efficient Perovskite Solar Cells at JoVE.com

Monovalent Cation Doping of CH3NH3PbI3 for Efficient Perovskite Solar Cells

Here, we present a protocol to adjust the properties of solution-processed CH3NH3PbI3 through the incorporation of monovalent cation additives in order to achieve highly efficient perovskite solar cells.

Monovalent Cation Doping of CH3NH3PbI3 for Efficient Perovskite Solar Cells

Here, we demonstrate the incorporation of monovalent cation additives into CH3NH3PbI3 perovskite in order to adjust the optical, excitonic, and electrical ...

monovalent-cation-doping-ch3nh3pbi3-for-efficient-perovskite-solar

Universidad de Cartagena UDEC

Research

JoVE Journal

Engineering

16.5K Views.  University of Cambridge. Here, we present a protocol to adjust the properties of solution-processed CH3NH3PbI3 through the incorporation of monovalent cation additives in order to achieve highly efficient perovskite solar cells.

Video: Monovalent Cation Doping of CH3NH3PbI3 for Efficient Perovskite Solar Cells

Fabrication of Fully Solution Processed Inorganic Nanocrystal Photovoltaic Devices

We demonstrate a method for the preparation of fully solution processed inorganic solar cells from a spin and spray coating deposition of nanocrystal inks. For the photoactive absorber layer, colloidal CdTe and CdSe nanocrystals (3-5 nm) are synthesized using an inert hot injection technique and cleaned with precipitations to remove excess starting reagents. Similarly, gold nanocrystals (3-5 nm) are synthesized under ambient conditions and dissolved in organic solvents. In addition, precursor solutions for transparent conductive indium tin oxide (ITO) films are prepared from solutions of indium and tin salts paired with a reactive oxidizer. Layer-by-layer, these solutions are deposited onto a glass substrate following annealing (200-400 &#176;C) to build the nanocrystal solar cell (glass/ITO/CdSe/CdTe/Au). Pre-annealing ligand exchange is required for CdSe and CdTe nanocrystals where films are dipped in NH4Cl:methanol to replace long-chain native ligands with small inorganic Cl- anions. NH4Cl(s) was found to act as a catalyst for the sintering reaction (as a non-toxic alternative to the conventional CdCl2(s) treatment) leading to grain growth (136&#177;39 nm) during heating. The thickness and roughness of the prepared films are characterized with SEM and optical profilometry. FTIR is used to determine the degree of ligand exchange prior to sintering, and XRD is used to verify the crystallinity and phase of each material. UV/Vis spectra show high visible light transmission through the ITO layer and a red shift in the absorbance of the cadmium chalcogenide nanocrystals after thermal annealing. Current-voltage curves of completed devices are measured under simulated one sun illumination. Small differences in deposition techniques and reagents employed during ligand exchange have been shown to have a profound influence on the device properties. Here, we examine the effects of chemical (sintering and ligand exchange agents) and physical treatments (solution concentration, spray-pressure, annealing time and annealing temperature) on photovoltaic device performance.

This protocol describes the synthesis and solution deposition of inorganic nanocrystals layer by layer to produce thin film electronics on non-conductive surfaces. Solvent-stabilized inks can produce complete photovoltaic devices on glass substrates via spin and spray coating following post-deposition ligand exchange and sintering.

We demonstrate a method for the preparation of fully solution processed inorganic solar cells from a spin and spray coating deposition of nanocrystal ...

Influence of Hybrid Perovskite Fabrication Methods on Film Formation, Electronic Structure, and Solar Cell Performance

Hybrid organic/inorganic halide perovskites have lately been a topic of great interest in the field of solar cell applications, with the potential to achieve device efficiencies exceeding other thin film device technologies. Yet, large variations in device efficiency and basic physical properties are reported. This is due to unintentional variations during film processing, which have not been sufficiently investigated so far. We therefore conducted an extensive study of the morphology and electronic structure of a large number of CH3NH3PbI3 perovskite where we show how the preparation method as well as the mixing ratio of educts methylammonium iodide and lead(II) iodide impact properties like film formation, crystal structure, density of states, energy levels, and ultimately the solar cell performance.

We present an extensive study on the effects of different fabrication methods for organic/inorganic perovskite thin films by comparing crystal structures, density of states, energy levels, and ultimately the solar cell performance.

Hybrid organic/inorganic halide perovskites have lately been a topic of great interest in the field of solar cell applications, with the potential to ...

Chemistry

Low Pressure Vapor-assisted Solution Process for Tunable Band Gap Pinhole-free Methylammonium Lead Halide Perovskite Films

Organo-lead halide perovskites have recently attracted great interest for potential applications in thin-film photovoltaics and optoelectronics. Herein, we present a protocol for the fabrication of this material via the low-pressure vapor assisted solution process (LP-VASP) method, which yields ~19% power conversion efficiency in planar heterojunction perovskite solar cells. First, we report the synthesis of methylammonium iodide (CH3NH3I) and methylammonium bromide (CH3NH3Br) from methylamine and the corresponding halide acid (HI or HBr). Then, we describe the fabrication of pinhole-free, continuous methylammonium-lead halide perovskite (CH3NH3PbX3 with X = I, Br, Cl and their mixture) films with the LP-VASP. This process is based on two steps: i) spin-coating of a homogenous layer of lead halide precursor onto a substrate, and ii) conversion of this layer to CH3NH3PbI3-xBrx by exposing the substrate to vapors of a mixture of CH3NH3I and CH3NH3Br at reduced pressure and 120 &#176;C. Through slow diffusion of the methylammonium halide vapor into the lead halide precursor, we achieve slow and controlled growth of a continuous, pinhole-free perovskite film. The LP-VASP allows synthetic access to the full halide composition space in CH3NH3PbI3-xBrx with 0&#160;&#8804; x&#160;&#8804; 3. Depending on the composition of the vapor phase, the bandgap can be tuned between 1.6 eV&#160;&#8804; Eg&#160;&#8804; 2.3 eV. In addition, by varying the composition of the halide precursor and of the vapor phase, we can also obtain CH3NH3PbI3-xClx. Films obtained from the LP-VASP are reproducible, phase pure as confirmed by X-ray diffraction measurements, and show high photoluminescence quantum yield. The process does not require the use of a glovebox.

Here, we present a protocol for the synthesis of CH3NH3I and CH3NH3Br precursors and the subsequent formation of pinhole-free, continuous CH3NH3PbI3-xBrx thin films for the application in high efficiency solar cells and other optoelectronic devices.

Organo-lead halide perovskites have recently attracted great interest for potential applications in thin-film photovoltaics and optoelectronics. Herein, ...

Recombination Dynamics in Thin-film Photovoltaic Materials via Time-resolved Microwave Conductivity

A method for investigating recombination dynamics of photo-induced charge carriers in thin film semiconductors, specifically in photovoltaic materials such as organo-lead halide perovskites is presented. The perovskite film thickness and absorption coefficient are initially characterized by profilometry and UV-VIS absorption spectroscopy. Calibration of both laser power and cavity sensitivity is described in detail. A protocol for performing Flash-photolysis Time Resolved Microwave Conductivity (TRMC) experiments, a non-contact method of determining the conductivity of a material, is presented. A process for identifying the real and imaginary components of the complex conductivity by performing TRMC as a function of microwave frequency is given. Charge carrier dynamics are determined under different excitation regimes (including both power and wavelength). Techniques for distinguishing between direct and trap-mediated decay processes are presented and discussed. Results are modelled and interpreted with reference to a general kinetic model of photoinduced charge carriers in a semiconductor. The techniques described are applicable to a wide range of optoelectronic materials, including organic and inorganic photovoltaic materials, nanoparticles, and conducting/semiconducting thin films.

A Time Resolved Microwave Conductivity technique for investigating direct and trap-mediated recombination dynamics and determining carrier mobilities of thin film semiconductors is presented here.

A method for investigating recombination dynamics of photo-induced charge carriers in thin film semiconductors, specifically in photovoltaic materials ...

Flash Infrared Annealing for Perovskite Solar Cell Processing

Organic&#8211;inorganic perovskites have an impressive potential for the design of next generation solar cells and are currently considered for upscaling and commercialization. Currently, perovskite solar cells rely on spin-coating which is neither practical for large areas nor environmentally friendly. Indeed, one of the conventional and most effective lab-scale methods to induce perovskite crystallization, the antisolvent method, requires an amount of toxic solvent that is difficult to apply on larger surfaces. To solve this problem, an antisolvent-free and rapid thermal annealing process called flash infrared annealing (FIRA) can be used to produce highly crystalline perovskite films. The FIRA oven is composed of an array of near-infrared halogen lamps with an illumination power of 3,000 kW/m2. A hollow aluminum body enables an effective water-cooling system. The FIRA method allows the synthesis of perovskite films in less than 2 s, achieving efficiencies &#62;20%. FIRA has a unique potential for the industry because it can be adapted to continuous processing, is antisolvent-free, and does not require lengthy, hour-long annealing steps.

We describe a flash infrared annealing method used for the synthesis of perovskite and mesoscopic-TiO2 films. Annealing parameters are varied and optimized for processing on fluorine-doped tin oxide (FTO) glass and indium tin oxide-coated polyethylene terephthalate (ITO PET), subsequently giving devices power conversion efficiencies &#62;20%.

Organic&#8211;inorganic perovskites have an impressive potential for the design of next generation solar cells and are currently considered for upscaling ...

Environment

Key Factors Affecting the Performance of Sb2S3-sensitized Solar Cells During an Sb2S3 Deposition via SbCl3-thiourea Complex Solution-processing

Sb2S3 is considered as one of the emerging light absorbers that can be applied to next-generation solar cells because of its unique optical and electrical properties. Recently, we demonstrated its potential as next-generation solar cells by achieving a high photovoltaic efficiency of &#62; 6% in Sb2S3-sensitized solar cells using a simple thiourea (TU)-based complex solution method. Here, we describe the key experimental procedures for the deposition of Sb2S3 on a mesoporous TiO2 (mp-TiO2) layer using a SbCl3-TU complex solution in the fabrication of solar cells. First, the SbCl3-TU solution is synthesized by dissolving SbCl3 and TU in N,N-dimethylformamide at different molar ratios of SbCl3:TU. Then, the solution is deposited on as-prepared substrates consisting of mp-TiO2/TiO2-blocking layer/F-doped SnO2 glass by spin coating. Finally, to form crystalline Sb2S3, the samples are annealed in an N2-filled glove box at 300 &#176;C. The effects of the experimental parameters on the photovoltaic device performance are also discussed.

Key Factors Affecting the Performance of Sb2S3-sensitized Solar Cells During an Sb2S3 Deposition via SbCl3-thiourea Complex Solution-processing

This work provides a detailed experimental procedure for the deposition of Sb2S3 on a mesoporous TiO2 layer using a SbCl3-thiourea complex solution for applications in Sb2S3-sensitized solar cells. This article also determines key factors governing the deposition process.

Sb2S3 is considered as one of the emerging light absorbers that can be applied to next-generation solar cells because of its unique optical and electrical ...

A Modular Microfluidic Technology for Systematic Studies of Colloidal Semiconductor Nanocrystals

Colloidal semiconductor nanocrystals, known as quantum dots (QDs), are a rapidly growing class of materials in commercial electronics, such as light emitting diodes (LEDs) and photovoltaics (PVs). Among this material group, inorganic/organic perovskites have demonstrated significant improvement and potential towards high-efficiency, low-cost PV fabrication due to their high charge carrier mobilities and lifetimes. Despite the opportunities for perovskite QDs in large-scale PV and LED applications, the lack of fundamental and comprehensive understanding of their growth pathways has inhibited their adaptation within continuous nanomanufacturing strategies. Traditional flask-based screening approaches are generally expensive, labor-intensive, and imprecise for effectively characterizing the broad parameter space and synthesis variety relevant to colloidal QD reactions. In this work, a fully autonomous microfluidic platform is developed to systematically study the large parameter space associated with the colloidal synthesis of nanocrystals in a continuous flow format. Through the application of a novel translating three-port flow cell and modular reactor extension units, the system may rapidly collect fluorescence and absorption spectra across reactor lengths ranging 3 - 196 cm. The adjustable reactor length not only decouples the residence time from the velocity-dependent mass transfer, it also substantially improves the sampling rates and chemical consumption due to the characterization of 40 unique spectra within a single equilibrated system. Sample rates may reach up to 30,000 unique spectra per day, and the conditions cover 4 orders of magnitude in residence times ranging 100 ms - 17 min. Further applications of this system would substantially improve the rate and precision of the material discovery and screening in future studies. Detailed within this report are the system materials and assembly protocols with a general description of the automated sampling software and offline data processing.

Detailed herein are the operation and assembly protocols of a modular microfluidic screening platform for the systematic characterization of colloidal semiconductor nanocrystal syntheses. Through fully adjustable system arrangements, highly efficient spectra collection may be carried out across 4 orders of magnitude reaction time scales within a mass transfer-controlled sampling space.

Colloidal semiconductor nanocrystals, known as quantum dots (QDs), are a rapidly growing class of materials in commercial electronics, such as light ...

Solution-Processed "Silver-Bismuth-Iodine" Ternary Thin Films for Lead-Free Photovoltaic Absorbers

Bismuth-based hybrid perovskites are regarded as promising photo-active semiconductors for environment-friendly and air-stable solar cell applications. However, poor surface morphologies and relatively high bandgap energies have limited their potential. Silver-bismuth-iodine (Ag-Bi-I) is a promising semiconductor for optoelectronic devices. Therefore, we demonstrate the fabrication of Ag-Bi-I ternary thin films using material solution processing. The resulting thin films exhibit controlled surface morphologies and optical bandgaps according to their thermal annealing temperatures. In addition, it has been reported that Ag-Bi-I ternary systems crystallize to AgBi2I7, Ag2BiI5, etc. according to the ratio of the precursor chemicals. The solution-processed AgBi2I7 thin films exhibit a cubic-phase crystal structure, dense, pinhole-free surface morphologies with grains ranging in size from 200 to 800 nm, and an indirect bandgap of 1.87 eV. The resultant AgBi2I7 thin films show good air stability and energy band diagrams, as well as surface morphologies and optical bandgaps suitable for lead-free and air-stable single-junction solar cells. Very recently, a solar cell with 4.3% power conversion efficiency was obtained by optimizing the Ag-Bi-I crystal compositions and solar cell device architectures.

Herein, we present detailed protocols for solution-processed silver-bismuth-iodine (Ag-Bi-I) ternary semiconductor thin films fabricated on TiO2-coated transparent electrodes and their potential application as air-stable and lead-free optoelectronic devices.

Bismuth-based hybrid perovskites are regarded as promising photo-active semiconductors for environment-friendly and air-stable solar cell applications. ...

Inkjet Printing All Inorganic Halide Perovskite Inks for Photovoltaic Applications

A method for synthesizing photoactive inorganic&#160;perovskite quantum dot inks and an inkjet printer deposition method, using the synthesized inks, are demonstrated. The ink synthesis is based on a simple wet chemical reaction and the inkjet printing protocol is a facile step by step method. The inkjet printed thin films have been characterized by X-ray diffraction, optical absorption spectroscopy, photoluminescent spectroscopy, and electronic transport measurements. X-ray diffraction of the printed quantum dot films indicates a crystal structure consistent with an orthorhombic room temperature phase with (001) orientation. In conjunction with other characterization methods, the X-ray diffraction&#160;measurements show high quality films can be obtained through the inkjet printing method.

A protocol for synthesizing inorganic-lead-halide hybrid perovskite quantum dot inks for inkjet printing and the protocol for preparing and printing the quantum dot inks in an inkjet printer with post characterization techniques are presented.

A method for synthesizing photoactive inorganic&#160;perovskite quantum dot inks and an inkjet printer deposition method, using the synthesized inks, are ...

Facile Synthesis of Colloidal Lead Halide Perovskite Nanoplatelets via Ligand-Assisted Reprecipitation

In this work, we demonstrate a facile method for colloidal lead halide perovskite nanoplatelet synthesis (Chemical formula: L2[ABX3]n-1BX4, L: butylammonium and octylammonium, A: methylammonium or formamidinium, B: lead, X: bromide and iodide, n: number of [BX6]4- octahedral layers in the direction of nanoplatelet thickness) via ligand-assisted reprecipitation. Individual perovskite precursor solutions are prepared by dissolving each nanoplatelet constituent salt in N,N-dimethylformamide (DMF), which is a polar organic solvent, and then mixing in specific ratios for targeted nanoplatelet thickness and composition. Once the mixed precursor solution is dropped into nonpolar toluene, the abrupt change in the solubility induces the instantaneous crystallization of nanoplatelets with surface-bound alkylammonium halide ligands providing colloidal stability. Photoluminescence and absorption spectra reveal emissive and strongly quantum-confined features. X-ray diffraction and transmission electron microscopy confirm the two-dimensional structure of the nanoplatelets. Furthermore, we demonstrate that the band gap of perovskite nanoplatelets can be continuously tuned in the visible range by varying the stoichiometry of the halide ion(s). Lastly, we demonstrate the flexibility of the ligand-assisted reprecipitation method by introducing multiple species as surface-capping ligands. This methodology represents a simple procedure for preparing dispersions of emissive 2D colloidal semiconductors.

This work demonstrates facile room-temperature synthesis of colloidal quantum-confined lead halide perovskite nanoplatelets by ligand-assisted reprecipitation method. Synthesized nanoplatelets show spectrally narrow optical features and continuous spectral tunability throughout the visible range by varying the composition and thicknesses.

Monovalent Cation Doping of CH₃NH₃PbI₃ for Efficient Perovskite Solar Cells

Podsumowanie

Przeglądaj więcej filmów

Rozdziały w tym wideo