The work described in this paper was supported by a grant from the CII-HK/PolyU Innovation Fund. Further support was provided by the Shenzhen Peacock Plan (KQTD2015071616442225) and the Chinese Government &#34;Thousand Talent&#34; Program (Y62HB31601). Also, the help from the Department of Applied Biology &#38; Chemical Technology of the Hong Kong Polytechnic University and the Hong Kong Polytechnic University Research Institute for Sustainable Urban Development (RISUD) is appreciated.

1. Pre-treatment of HGM
<ol>
	<li>Place the HGM into a 500-mL beaker with 200 mL of absolute alcohol; the low density of unbroken HGM causes it to suspend in the alcohol, but because the density of broken HGM is larger than that of alcohol, it precipitates in the solution. After 30 min, collect the suspended HGM using a clean spoon and dry at 80 &#176;C in an oven for further application.</li>
</ol>
2. Synthesis of MCHGM
<ol>
	<li>Place 5 g of unbroken HGM, 47.5 mL of ethanol, and 2.5 mL of DI water in a three-necked flask. Stir using a mixing motor at 400 r/min for 20 min (pre-mixing).</li>
	<li>Mix 15 g of TBT, 1 g of PFOTES, and 30 mL of absolute alcohol in a 200-mL beaker. Pour the mixture into a constant-pressure funnel.</li>
	<li>Insert the constant-pressure funnel into one of the holes of the three-necked flask. Drop the mixture contained in the constant-pressure funnel into the three-necked flask at a speed of 1 drop per 7 s, which is achieved by adjusting the valve of the constant-pressure funnel. Continue the reaction for 3 h.</li>
	<li>Pour the mixture from the three-necked flask into a hydrothermal reactor. Put the sealed reactor in a suitable steel sleeve in a 180 &#176;C oven for 6 h. 
	NOTE: Make sure that the reactor has a suitable cover. After it is covered, put the reactor into the steel sleeve. The sleeve should also be sealed with a cover.</li>
	<li>After the reaction is over, collect the samples suspended in the hydrothermal reactor using a big spoon. Dry the samples at 80 &#176;C for 4 h to obtain MCHGM.</li>
</ol>
3. Synthesis of F-SCHGM
<ol>
	<li>Add 5 g of unbroken HGM, 47.5 mL of absolute ethanol, and 2.5 mL of DI water to a three-necked flask. Stir using a mixing motor at 400 r/min for 20 min (pre-mixing). Mix 1 g of PFOTES and 30 mL of absolute ethanol in a 200-mL beaker. Transfer the PFOTES and absolute ethanol mixture to a constant-pressure funnel.</li>
	<li>Insert the constant-pressure funnel into the three-necked flask. Drop the mixture contained in the constant-pressure funnel into the three-necked flask at a speed of 1 drop per 7 s. Let the reaction run for 3 h.</li>
	<li>Transfer the mixture from the three-necked flask to a hydrothermal reactor. Put the sealed reactor in a 180 &#176;C oven for 6 h. After the reaction is over, collect the samples suspended in the hydrothermal reactor using a big spoon. Dry the samples at 80 &#176;C for 4 h to obtain F-SCHGM.</li>
</ol>
4. Synthesis of Ti-SCHGM
<ol>
	<li>Place 5 g of unbroken HGM, 47.5 mL of absolute ethanol, and 2.5 mL of DI water in a three-necked flask. Stir at 400 r/min for 20 min (pre-mixing). Mix 15 g of TBT and 30 mL of absolute ethanol in a 200-mL beaker. Transfer the TBT and absolute ethanol mixture to a constant-pressure funnel.</li>
	<li>Insert the constant-pressure funnel into the three-necked flask. Drop the mixture in the constant-pressure funnel into the three-necked flask at a speed of 1 drop per 7 s. Let the reaction run for 3 h.</li>
	<li>Transfer the mixture from the three-necked flask to a hydrothermal reactor. Put the sealed reactor in a 180 &#176;C oven for 6 h. Collect the samples in the hydrothermal reactor after the reaction is over. Dry the samples at 80 &#176;C for 4 h to obtain Ti-SCHGM.</li>
</ol>
5. Characterizations
<ol>
	<li>Conduct XRD characterizations on all samples. Collect the data using a highly versatile, multipurpose X-ray diffraction system with Cu K&#945; radiation (&#955; = 0.15406 nm) and a 2&#952; ranging from 10&#176; to 80&#176;.</li>
	<li>Acquire scanning electron microscope20,21 images after spraying the samples with gold. During the SEM tests, conduct the EDS is on a specific area.</li>
	<li>Measure the contact angle by using a contact-angle goniometer22; the water drop volume should be 10 &#181;L.</li>
	<li>Measure the sliding angle23 by changing the tilt angle of the surface. Minimize the angle until the water drop can just slide down.
	<ol>
		<li>Stick double-sided tape on a glass sheet (size: 26 mm x 76 mm x 2 mm). Using a spoon, uniformly place the powders (F-SCHGM or MCHGM) on the tape. Using an injector, add a water drop (volume: 0.05 mL) to the powder surface.</li>
		<li>Put the glass sheet on the motor platform of the contact-angle goniometer. Tilt the glass sheet by leaning the motor platform at a rate of 1&#176;/s. Stop the motor when the water drop starts to slide; the tilt angle is the sliding angle.</li>
	</ol>
	</li>
	<li>Measure the reflectivity spectra using a spectrophotometer24. NOTE: The wavelength is from 450 nm to 2,550 nm.</li>
	<li>Measure the thermal conductivity of all samples using a thermal conductivity meter25.</li>
</ol>

<ol>
	<li>Yung, K. C., Zhu, B. L., Yue, T. M., Xie, C. S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Preparation+and+properties+of+hollow+glass+microsphere-filled+epoxy-matrix+composites.">Preparation and properties of hollow glass microsphere-filled epoxy-matrix composites.</a> Compos. Sci. Technol. 69 (2), 260-264 (2008).</li><li>Xu, N., Dai, J., Zhu, Z., Huang, X., Wu, P. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Synthesis+and+characterization+of+hollow+glass-ceramics+microspheres.">Synthesis and characterization of hollow glass-ceramics microspheres.</a> Compos. Sci. Technol. 72 (4), 528-532 (2011).</li><li>Li, B., Yuan, J., An, Z., Zhang, J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Effect+of+microstructure+and+physical+parameters+of+hollow+glass+microsphere+on+insulation+performance.">Effect of microstructure and physical parameters of hollow glass microsphere on insulation performance.</a> Mater. Lett. 65 (12), 1992-1994 (2011).</li><li>Hu, Y., Mei, R., An, Z., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Silicon+rubber/hollow+glass+microsphere+composites:+Influence+of+broken+hollow+glass+microsphere+on+mechanical+and+thermal+insulation+property.">Silicon rubber/hollow glass microsphere composites: Influence of broken hollow glass microsphere on mechanical and thermal insulation property.</a> Compos. Sci. Technol. 79, 64-69 (2013).</li><li>Geleil, A. S., Hall, M. M., Shelby, J. E. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Hollow+glass+microspheres+for+use+in+radiation+shielding.">Hollow glass microspheres for use in radiation shielding.</a> J. Non-Cryst. Solids. 352, 620-625 (2006).</li><li>Khimiya. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=.">.</a> Handbook of Fillers for Polymeric Composite Materials [Russian translation]. , (1981).</li><li>Greiner-Bar, G. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=HoNe+Mikroglaskugeln.+Herstellung,+Eigenschaften+und+Anwendung.">HoNe Mikroglaskugeln. Herstellung, Eigenschaften und Anwendung.</a> Silikattechnik. 40 (1), 23-25 (1989).</li><li>Kool, L. B. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Method+for+storing+hydrogen,+and+related+articles+and+systems.">Method for storing hydrogen, and related articles and systems.</a> United States Patent. , (2010).</li><li>Brow, R. K., Schmitt, M. L. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=A+survey+of+energy+and+environmental+application+of+glass.">A survey of energy and environmental application of glass.</a> J. Eur. Ceram. Soc. 29, 1193-1201 (2009).</li><li>Awaja, F., Arhatari, B. D. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=X-ray+Micro+Computed+Tomography+investigation+of+accelerated+thermal+degradation+of+epoxy+resin/glass+microsphere+syntactic+foam.">X-ray Micro Computed Tomography investigation of accelerated thermal degradation of epoxy resin/glass microsphere syntactic foam.</a> Composites Part A. 40 (8), 1217-1222 (2009).</li><li>Wang, S., Luo, R., Ni, Y. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Preparation+and+characterization+of+resin-derived+carbon+foams+reinforced+by+hollow+ceramic+microspheres.">Preparation and characterization of resin-derived carbon foams reinforced by hollow ceramic microspheres.</a> Mater. Sci. Eng., A. 527 (15), 3392-3395 (2010).</li><li>Carp, O., Huisman, C. L., Reller, A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Photoinduced+reactivity+of+titanium+dioxide.">Photoinduced reactivity of titanium dioxide.</a> Prog. Solid State Chem. 32 (1), 33-177 (2004).</li><li>Fujishima, A., Rao, T. N., Tryk, D. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Titanium+dioxide+photocatalysis.">Titanium dioxide photocatalysis.</a> J. Photochem. Photobiol. C. 1 (1), 1-21 (2000).</li><li>Fujishima, A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Electrochemical+photolysis+of+water+at+a+semiconductor+electrode.">Electrochemical photolysis of water at a semiconductor electrode.</a> Nature. 238 (5358), 37-38 (1972).</li><li>Hoffmann, M. R., Martin, S. T., Choi, W., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Environmental+applications+of+semiconductor+photocatalysis.">Environmental applications of semiconductor photocatalysis.</a> Chem. Rev. 95 (1), 69-96 (1995).</li><li>Chen, X., Mao, S. S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Titanium+dioxide+nanomaterials:+synthesis,+properties,+modifications,+and+applications.">Titanium dioxide nanomaterials: synthesis, properties, modifications, and applications.</a> Chem. Rev. 107 (7), 2891-2959 (2007).</li><li>Yuan, J., An, Z., Li, B., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Facile+aqueous+synthesis+and+thermal+insulating+properties+of+low-density+glass/TiO2+core/shell+composite+hollow+spheres.">Facile aqueous synthesis and thermal insulating properties of low-density glass/TiO2 core/shell composite hollow spheres.</a> Particuology. 10 (4), 475-479 (2012).</li><li>Yan, H., Yuanhao, W., Hongxing, Y. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=TEOS/silane+coupling+agent+composed+double+layers+structure:+A+novel+super-hydrophilic+coating+with+controllable+water+contact+angle+value.">TEOS/silane coupling agent composed double layers structure: A novel super-hydrophilic coating with controllable water contact angle value.</a> Appl. Energy. , (2015).</li><li>Wang, Y., Yang, H., Lu, L. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Three-dimensional+double+deck+meshlike+dye-sensitized+solar+cells.">Three-dimensional double deck meshlike dye-sensitized solar cells.</a> J. Appl. Phys. 108 (6), 064510 (2010).</li><li>Wang, Y., Yang, H., Xu, H. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=DNA-like+dye-sensitized+solar+cells+based+on+TiO+2+nanowire-covered+nanotube+bilayer+film+electrodes.">DNA-like dye-sensitized solar cells based on TiO 2 nanowire-covered nanotube bilayer film electrodes.</a> Mater. Lett. 64 (2), 164-166 (2010).</li><li>Wang, Y., Lu, L., Yang, H., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Development+of+high+dispersed+TiO2+paste+for+transparent+screen-printable+self-cleaning+coatings+on+glass.">Development of high dispersed TiO2 paste for transparent screen-printable self-cleaning coatings on glass.</a> J. Nanopart. Res. 15 (1), 1-6 (2013).</li><li>Kwok, D. Y., Neumann, A. W. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Contact+angle+measurement+and+contact+angle+interpretation.">Contact angle measurement and contact angle interpretation.</a> Adv. Colloid Interface Sci. 81 (3), 167-249 (1999).</li><li>Pierce, E., Carmona, F. J., Amirfazli, A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Understanding+of+sliding+and+contact+angle+results+in+tilted+plate+experiments.">Understanding of sliding and contact angle results in tilted plate experiments.</a> Colloids Surf., A. 323 (1), 73-82 (2008).</li><li>Kim, W. S., Kim, T. H., Kim, E. S., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Microwave+dielectric+properties+and+far+infrared+reflectivity+spectra+of+the+(Zr0.+8Sn0.+2)+TiO4+ceramics+with+additives.">Microwave dielectric properties and far infrared reflectivity spectra of the (Zr0. 8Sn0. 2) TiO4 ceramics with additives.</a> Jpn. J. Appl. Phys. 37 (9S), 5367 (1998).</li><li>Hasselman, D. P. H., Johnson, L. F. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Effective+thermal+conductivity+of+composites+with+interfacial+thermal+barrier+resistance.">Effective thermal conductivity of composites with interfacial thermal barrier resistance.</a> J. Compos. Mater. 21 (6), 508-515 (1987).</li><li>Cassie, A. B. D., Baxter, S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Wettability+of+porous+surfaces.">Wettability of porous surfaces.</a> Trans. Faraday Soc. 40, 546-551 (1944).</li><li>Wenzel, R. N. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Resistance+of+solid+surfaces+to+wetting+by+water.">Resistance of solid surfaces to wetting by water.</a> Ind. Eng. Chem. Res. 28 (8), 988-994 (1936).</li><li>Shirtcliffe, N. J., McHale, G., Newton, M. I., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Intrinsically+superhydrophobic+organosilica+sol-gel+foams.">Intrinsically superhydrophobic organosilica sol-gel foams.</a> Langmuir. 19 (14), 5626-5631 (2003).</li><li>Rothstein, J. P. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Slip+on+superhydrophobic+surfaces.">Slip on superhydrophobic surfaces.</a> Annu. Rev. Fluid Mech. 42, 89-109 (2010).</li><li>Rodo&#353;ek, M., Kreta, A., Gaber&#353;&#269;ek, M., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Ex+situ+IR+reflection-absorption+and+in+situ+AFM+electrochemical+characterisation+of+the+1,+2-bis+(trimethoxysilyl)+ethane-based+protective+coating+on+AA+2024+alloy.">Ex situ IR reflection-absorption and in situ AFM electrochemical characterisation of the 1, 2-bis (trimethoxysilyl) ethane-based protective coating on AA 2024 alloy.</a> Corros. Sci. 102, 186-199 (2016).</li><li>Jiang, J., Zhang, J., Zhu, P., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=High+pressure+studies+of+Ni+3[(C+2+H+5+N+5)+6+(H+2+O)+6](NO+3)+6·+1.5+H+2+O+by+Raman+scattering,+IR+absorption,+and+synchrotron+X-ray+diffraction.">High pressure studies of Ni 3[(C 2 H 5 N 5) 6 (H 2 O) 6](NO 3) 6· 1.5 H 2 O by Raman scattering, IR absorption, and synchrotron X-ray diffraction.</a> RSC Adv. 6 (69), 65031-65037 (2016).</li><li>Arukalam, I. O., Oguzie, E. E., Li, Y. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Fabrication+of+FDTS-modified+PDMS-ZnO+nanocomposite+hydrophobic+coating+with+anti-fouling+capability+for+corrosion+protection+of+Q235+steel.">Fabrication of FDTS-modified PDMS-ZnO nanocomposite hydrophobic coating with anti-fouling capability for corrosion protection of Q235 steel.</a> Journal of Colloid and Interface Science. 484, 220-228 (2016).</li><li>Hou, W., Xiao, Y., Han, G., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Serrated,+flexible+and+ultrathin+polyaniline+nanoribbons:+An+efficient+counter+electrode+for+the+dye-sensitized+solar+cell.">Serrated, flexible and ultrathin polyaniline nanoribbons: An efficient counter electrode for the dye-sensitized solar cell.</a> J. Power Sources. 322, 155-162 (2016).</li></ol>

The authors have nothing to disclose.

In this manuscript, the critical step in the protocol is the hydrothermal process. It influences the formation of TiO2, the final reflectivity, and the superhydrophobicity. The temperature control and reaction time are also quite significant. If the reaction conditions change, the final products can be flawed.
This method provides a simple way to synthesize superhydrophobic and highly IR-reflective HGM in one step. In previous research, the superhydrophobic and reflectivity properti...

Hollow glass microspheres (HGM) are inorganic materials ranging in size from 10 to 100 &#181;m. They demonstrate many useful features, such as excellent dispersion, high flow ability, low density, and superior thermal insulation properties1,2,3,4. Because of their hollow structure, HGM have an extremely low thermal conductivity10,11. For these reasons, they are applied in many areas, including aerospace engineering5, deep-sea exploration6,7, hydrogen storage8,9, etc. However, they still demonstrate some disadvantages, such as low strength. In addition, IR light is able to transmit through HGM and heat the subject behind. Therefore, surface modifications on HGM are essential to reduce the radiative thermal transfer. An effective method is to coat an IR-blocking material onto the HGM surface. As a semiconductor, TiO2 has been used in many areas, such as photo-catalysis12,13, solar cell development, sensor fabrication14, environmental applications15, and energy storage16. In addition, it also shows low emissivity in the visible light and infrared band17,18,19. Therefore, for our purposes, TiO2 was a prudent selection due to its relatively low price and high performance.
However, the coating is quite easy for pollutants to foul, which seriously affects the reflectivity of TiO2. The reflectivity must reduce gradually. Therefore, a self-cleaning coating is essential to prevent the coating from fouling and to prolong the working time of such a coating.
In this manuscript, a soft-chemistry method was used to develop superhydrophobic TiO2-coated HGM. Tetrabutyl titanate (TBT) and 1H,1H,2H,2H-perfluorooctyltriethoxysilane (PFOTES) were selected as the Ti source and superhydrophobic agent, respectively. They were hydrolyzed and deposited on the HGM surface. Then, after the hydrothermal process, the anatase TiO2 formed on the HGM surface, and the superhydrophobic properties remained. For comparison, PFOTES single-coated HGM (F-SCHGM) and TiO2 single-coated HGM (Ti-SCHGM) were synthesized as well. The synthesis scheme is shown in Figure 1.

<table><tbody><tr><td>HGM</td><td>Technical Institute of Physics and Chemistry, Chinese Academy of Science</td><td>N/A</td><td>N/A</td></tr><tr><td>TBT</td><td>Sigma-Aldrich</td><td>CAS#: 5593-70-4</td><td>Analytical grade</td></tr><tr><td>Ethyl Alcohol</td><td>Sigma-Aldrich</td><td>CAS#: 64-17-5</td><td>Analytical grade</td></tr><tr><td>PFOTES</td><td>Sigma-Aldrich</td><td>CAS#: 51851-37-7</td><td>98%</td></tr></tbody></table>

tio2-coated hollow glass microspheres with superhydrophobic and high ir-reflective properties synthesized by a soft-chemistry method

This manuscript proposes a soft-chemistry method to develop superhydrophobic and highly IR-reflective hollow glass microspheres (HGM). The anatase TiO2 and a superhydrophobic agent were coated on the HGM surface in one step. TBT and PFOTES were selected as the Ti source and the superhydrophobic agent, respectively. They were both coated on the HGM, and after the hydrothermal process, the TBT turned to anatase TiO2. In this way, a PFOTES/TiO2-coated HGM (MCHGM) was prepared. For comparison, PFOTES single-coated HGM (F-SCHGM) and TiO2 single-coated HGM (Ti-SCHGM) were synthesized as well. The PFOTES and TiO2 coatings on the HGM surface were demonstrated through X-ray diffraction (XRD), scanning electron microscopy (SEM), and energy-dispersive detector (EDS) characterizations. The MCHGM showed a higher contact angle (153&#176;) but a lower sliding angle (16&#176;) than F-SCHGM, with a contact angle of 141.2&#176; and a sliding angle of 67&#176;. In addition, both Ti-SCHGM and MCHGM displayed similar IR reflectivity values, which were about 5.8% higher than the original HGM and F-SCHGM. Also, the PFOTES coating barely changed the thermal conductivity. Therefore, F-SCHGM, with a thermal conductivity of 0.0479 W/(m&#183;K), was quite like the original HGM, which was 0.0475 W/(m&#183;K). MCHGM and Ti-SCHGM were also similar. Their thermal conductivity values were 0.0543 W/(m&#183;K) and 0.0543 W/(m&#183;K), respectively. The TiO2 coating slightly increased the thermal conductivity, but with the increase in reflectivity, the overall heat-insulation property was enhanced. Finally, since the IR-reflecting property is provided by the HGM coating, if the coating is fouled, the reflectivity decreases. Therefore, with the superhydrophobic coating, the surface is protected from fouling, and its lifetime is also prolonged.

The tests in step 4.4 reveal many features and properties of the samples. The XRD (Figure 2) reflects the formation of anatase TiO2. The SEM (Figure 3) and EDS (Figure 4) display the TiO2 and PFOTES that are coated on the HGM surface. The contact angle (Figure 5) and sliding angle (Figure 6) tests represent the superhydrophobicity. The Vis-NIR transmittance test (Figure 8</st...

Watch this Scientific Journal Video about TiO2-coated Hollow Glass Microspheres with Superhydrophobic and High IR-reflective Properties Synthesized by a Soft-chemistry Method at JoVE.com

TiO2-coated Hollow Glass Microspheres with Superhydrophobic and High IR-reflective Properties Synthesized by a Soft-chemistry Method

This manuscript proposes a soft-chemistry method to synthesize superhydrophobic, TiO2-coated hollow glass microspheres (HGM) with high IR-reflective properties.

TiO2-coated Hollow Glass Microspheres with Superhydrophobic and High IR-reflective Properties Synthesized by a Soft-chemistry Method

This manuscript proposes a soft-chemistry method to develop superhydrophobic and highly IR-reflective hollow glass microspheres (HGM). The anatase TiO2 ...

tio2-coated-hollow-glass-microspheres-with-superhydrophobic-high-ir

Universidad de Cartagena UDEC

Research

JoVE Journal

Chemistry

10.0K Views.  City University of Hong Kong. This manuscript proposes a soft-chemistry method to synthesize superhydrophobic, TiO2-coated hollow glass microspheres (HGM) with high IR-reflective properties.

Video: TiO2-coated Hollow Glass Microspheres with Superhydrophobic and High IR-reflective Properties Synthesized by a Soft-chemistry Method

Fabrication of Silica Ultra High Quality Factor Microresonators

Whispering gallery resonant cavities confine light in circular orbits at their periphery.1-2 The photon storage lifetime in the cavity, quantified by the quality factor (Q) of the cavity, can be in excess of 500ns for cavities with Q factors above 100 million. As a result of their low material losses, silica microcavities have demonstrated some of the longest photon lifetimes to date1-2. Since a portion of the circulating light extends outside the resonator, these devices can also be used to probe the surroundings. This interaction has enabled numerous experiments in biology, such as single molecule biodetection and antibody-antigen kinetics, as well as discoveries in other fields, such as development of ultra-low-threshold microlasers, characterization of thin films, and cavity quantum electrodynamics studies.3-7
The two primary silica resonant cavity geometries are the microsphere and the microtoroid. Both devices rely on a carbon dioxide laser reflow step to achieve their ultra-high-Q factors (Q&gt;100 million).1-2,8-9 However, there are several notable differences between the two structures. Silica microspheres are free-standing, supported by a single optical fiber, whereas silica microtoroids can be fabricated on a silicon wafer in large arrays using a combination of lithography and etching steps. These differences influence which device is optimal for a given experiment.
Here, we present detailed fabrication protocols for both types of resonant cavities. While the fabrication of microsphere resonant cavities is fairly straightforward, the fabrication of microtoroid resonant cavities requires additional specialized equipment and facilities (cleanroom). Therefore, this additional requirement may also influence which device is selected for a given experiment.
Introduction
An optical resonator efficiently confines light at specific wavelengths, known as the resonant wavelengths of the device. 1-2 The common figure of merit for these optical resonators is the quality factor or Q. This term describes the photon lifetime (&tau;o) within the resonator, which is directly related to the resonator's optical losses. Therefore, an optical resonator with a high Q factor has low optical losses, long photon lifetimes, and very low photon decay rates (1/&tau;o). As a result of the long photon lifetimes, it is possible to build-up extremely large circulating optical field intensities in these devices. This very unique property has allowed these devices to be used as laser sources and integrated biosensors.10
A unique sub-class of resonators is the whispering gallery mode optical microcavity. In these devices, the light is confined in circular orbits at the periphery. Therefore, the field is not completely confined within the device, but evanesces into the environment. Whispering gallery mode optical cavities have demonstrated some of the highest quality factors of any optical resonant cavity to date.9,11 Therefore, these devices are used throughout science and engineering, including in fundamental physics studies and in telecommunications as well as in biodetection experiments. 3-7,12
Optical microcavities can be fabricated from a wide range of materials and in a wide variety of geometries. A few examples include silica and silicon microtoroids, silicon, silicon nitride, and silica microdisks, micropillars, and silica and polymer microrings.13-17 The range in quality factor (Q) varies as dramatically as the geometry. Although both geometry and high Q are important considerations in any field, in many applications, there is far greater leverage in boosting device performance through Q enhancement. Among the numerous options detailed previously, the silica microsphere and the silica microtoroid resonator have achieved some of the highest Q factors to date.1,9 Additionally, as a result of the extremely low optical loss of silica from the visible through the near-IR, both microspheres and microtoroids are able to maintain their Q factors over a wide range of testing wavelengths.18 Finally, because silica is inherently biocompatible, it is routinely used in biodetection experiments.
In addition to high material absorption, there are several other potential loss mechanisms, including surface roughness, radiation loss, and contamination loss.2 Through an optimization of the device size, it is possible to eliminate radiation losses, which arise from poor optical field confinement within the device. Similarly, by storing a device in an appropriately clean environment, contamination of the surface can be minimized. Therefore, in addition to material loss, surface scattering is the primary loss mechanism of concern.2,8
In silica devices, surface scattering is minimized by using a laser reflow technique, which melts the silica through surface tension induced reflow. While spherical optical resonators have been studied for many years, it is only with recent advances in fabrication technologies that researchers been able to fabricate high quality silica optical toroidal microresonators (Q&gt;100 million) on a silicon substrate, thus paving the way for integration with microfluidics.1
The present series of protocols details how to fabricate both silica microsphere and microtoroid resonant cavities. While silica microsphere resonant cavities are well-established, microtoroid resonant cavities were only recently invented.1 As many of the fundamental methods used to fabricate the microsphere are also used in the more complex microtoroid fabrication procedure, by including both in a single protocol it will enable researchers to more easily trouble-shoot their experiments.

We describe the use of a carbon dioxide laser reflow technique to fabricate silica resonant cavities, including free-standing microspheres and on-chip microtoroids. The reflow method removes surface imperfections, allowing long photon lifetimes within both devices. The resulting devices have ultra high quality factors, enabling applications ranging from telecommunications to biodetection.

Whispering gallery resonant cavities confine light in circular orbits at their periphery.1-2 The photon storage lifetime in the cavity, quantified by the ...

Engineering

Harvesting Solar Energy by Means of Charge-Separating Nanocrystals and Their Solids

Conjoining different semiconductor materials in a single nano-composite provides synthetic means for the development of novel optoelectronic materials offering a superior control over the spatial distribution of charge carriers across material interfaces. As this study demonstrates, a combination of donor-acceptor nanocrystal (NC) domains in a single nanoparticle can lead to the realization of efficient photocatalytic1-5 materials, while a layered assembly of donor- and acceptor-like nanocrystals films gives rise to photovoltaic materials.
Initially the paper focuses on the synthesis of composite inorganic nanocrystals, comprising linearly stacked ZnSe, CdS, and Pt domains, which jointly promote photoinduced charge separation. These structures are used in aqueous solutions for the photocatalysis of water under solar radiation, resulting in the production of H2 gas. To enhance the photoinduced separation of charges, a nanorod morphology with a linear gradient originating from an intrinsic electric field is used5. The inter-domain energetics are then optimized to drive photogenerated electrons toward the Pt catalytic site while expelling the holes to the surface of ZnSe domains for sacrificial regeneration (via methanol). Here we show that the only efficient way to produce hydrogen is to use electron-donating ligands to passivate the surface states by tuning the energy level alignment at the semiconductor-ligand interface. Stable and efficient reduction of water is allowed by these ligands due to the fact that they fill vacancies in the valence band of the semiconductor domain, preventing energetic holes from degrading it. Specifically, we show that the energy of the hole is transferred to the ligand moiety, leaving the semiconductor domain functional. This enables us to return the entire nanocrystal-ligand system to a functional state, when the ligands are degraded, by simply adding fresh ligands to the system4.
To promote a photovoltaic charge separation, we use a composite two-layer solid of PbS and TiO2 films. In this configuration, photoinduced electrons are injected into TiO2 and are subsequently picked up by an FTO electrode, while holes are channeled to a Au electrode via PbS layer6. To develop the latter we introduce a Semiconductor Matrix Encapsulated Nanocrystal Arrays (SMENA) strategy, which allows bonding PbS NCs into the surrounding matrix of CdS semiconductor. As a result, fabricated solids exhibit excellent thermal stability, attributed to the heteroepitaxial structure of nanocrystal-matrix interfaces, and show compelling light-harvesting performance in prototype solar cells7.

A general strategy for the development of charge-separating semiconductor nanocrystal composites deployable for solar energy production is presented. We show that assembly of donor-acceptor nanocrystal domains in a single nanoparticle geometry gives rise to a photocatalytic function, while bulk-heterojunctions of donor-acceptor nanocrystal films can be used for photovoltaic energy conversion.

Conjoining different semiconductor materials in a single nano-composite provides synthetic means for the development of novel optoelectronic materials ...

Synthesis and Characterization of Supramolecular Colloids

Control over colloidal assembly is of utmost importance for the development of functional colloidal materials with tailored structural and mechanical properties for applications in photonics, drug delivery and coating technology. Here we present a new family of colloidal building blocks, coined supramolecular colloids, whose self-assembly is controlled through surface-functionalization with a benzene-1,3,5-tricarboxamide (BTA) derived supramolecular moiety. Such BTAs interact via directional, strong, yet reversible hydrogen-bonds with other identical BTAs. Herein, a protocol is presented that describes how to couple these BTAs to colloids and how to quantify the number of coupling sites, which determines the multivalency of the supramolecular colloids. Light scattering measurements show that the refractive index of the colloids is almost matched with that of the solvent, which strongly reduces the van der Waals forces between the colloids. Before photo-activation, the colloids remain well dispersed, as the BTAs are equipped with a photo-labile group that blocks the formation of hydrogen-bonds. Controlled deprotection with UV-light activates the short-range hydrogen-bonds between the BTAs, which triggers the colloidal self-assembly. The evolution from the dispersed state to the clustered state is monitored by confocal microscopy. These results are further quantified by image analysis with simple routines using ImageJ and Matlab. This merger of supramolecular chemistry and colloidal science offers a direct route towards light- and thermo-responsive colloidal assembly encoded in the surface-grafted monolayer.

A protocol for the synthesis and characterization of colloids coated with supramolecular moieties is described. These supramolecular colloids undergo self-assembly upon the activation of the hydrogen-bonds between the surface-anchored molecules by UV-light.

Control over colloidal assembly is of utmost importance for the development of functional colloidal materials with tailored structural and mechanical ...

Fabrication of Polymer Microspheres for Optical Resonator and Laser Applications

This paper describes three methods of preparing fluorescent microspheres comprising &#960;-conjugated or non-conjugated polymers: vapor diffusion, interface precipitation, and mini-emulsion. In all methods, well-defined, micrometer-sized spheres are obtained from a self-assembling process in solution. The vapor diffusion method can result in spheres with the highest sphericity and surface smoothness, yet the types of the polymers able to form these spheres are limited. On the other hand, in the mini-emulsion method, microspheres can be made from various types of polymers, even from highly crystalline polymers with coplanar, &#960;-conjugated backbones. The photoluminescent (PL) properties from single isolated microspheres are unusual: the PL is confined inside the spheres, propagates at the circumference of the spheres via the total internal reflection at the polymer/air interface, and self-interferes to show sharp and periodic resonant PL lines. These resonating modes are so-called "whispering gallery modes" (WGMs). This work demonstrates how to measure WGM PL from single isolated spheres using the micro-photoluminescence (&#181;-PL) technique. In this technique, a focused laser beam irradiates a single microsphere, and the luminescence is detected by a spectrometer. A micromanipulation technique is then used to connect the microspheres one by one and to demonstrate the intersphere PL propagation and color conversion from coupled microspheres upon excitation at the perimeter of one sphere and detection of PL from the other microsphere. These techniques, &#181;-PL and micromanipulation, are useful for experiments on micro-optic application using polymer materials.

Protocols for the synthesis of microspheres from polymers, the manipulation of microspheres, and micro-photoluminescence measurements are presented.

This paper describes three methods of preparing fluorescent microspheres comprising &#960;-conjugated or non-conjugated polymers: vapor diffusion, ...

Synthesizing Sodium Tungstate and Sodium Molybdate Microcapsules via Bacterial Mineral Excretion

We present a method, the bacterial mineral excretion (BME), for synthesizing two kinds of microcapsules, sodium tungstate and sodium molybdate, and the two metal oxides&#39; corresponding nanoparticles&#8212;the former being as small as 22 nm and the latter 15 nm. We fed two strains of bacteria, Shewanella algae and Pandoraea sp., with various concentrations of tungstate or molybdate ions. The concentrations of tungstate and molybdate were adjusted to make microcapsules of different length-to-diameter ratios. We found that the higher the concentration the smaller the nanoparticles were. The nanoparticles came in with three length-to-diameter ratios: 10:1, 3:1 and 1:1, which were achieved by feeding the bacteria respectively with a low concentration, a medium concentration, and a high concentration. The images of the hollow microcapsules were taken via the scanning electron microsphere (SEM). Their crystal structures were verified by X-ray diffraction (XRD)&#8212;the crystal structure of molybdate microcapsules is Na2MoO4 and that of tungstate microcapsules is Na2WO4 with Na2W2O7. These syntheses all were accomplished under a near ambient condition.

This work presents a protocol for manufacture sodium tungstate and sodium molybdate microcapsules via bacteria and their corresponding nanoparticles.

We present a method, the bacterial mineral excretion (BME), for synthesizing two kinds of microcapsules, sodium tungstate and sodium molybdate, and the ...

Fabrication of Superhydrophobic Metal Surfaces for Anti-Icing Applications

Several ways to produce superhydrophobic metal surfaces are presented in this work. Aluminum was chosen as the metal substrate due to its wide use in industry. The wettability of the produced surface was analyzed by bouncing drop experiments and the topography was analyzed by confocal microscopy. In addition, we show various methodologies to measure its durability and anti-icing properties. Superhydrophobic surfaces hold a special texture that must be preserved to keep their water-repellency. To fabricate durable surfaces, we followed two strategies to incorporate a resistant texture. The first strategy is a direct incorporation of roughness to the metal substrate by acid etching. After this surface texturization, the surface energy was decreased by silanization or fluoropolymer deposition. The second strategy is the growth of a ceria layer (after surface texturization) that should enhance the surface hardness and corrosion resistance. The surface energy was decreased with a stearic acid film.
The durability of the superhydrophobic surfaces was examined by a particle impact test, mechanical wear by lateral abrasion, and UV-ozone resistance. The anti-icing properties were explored by studying the ability to repeal subcooled water, freezing delay, and ice adhesion.

We illustrate several methodologies to produce superhydrophobic metal surfaces and to explore their durability and anti-icing properties.

Several ways to produce superhydrophobic metal surfaces are presented in this work. Aluminum was chosen as the metal substrate due to its wide use in ...

Photopatterning Proteins and Cells in Aqueous Environment Using TiO2 Photocatalysis

Organic contaminants adsorbed on the surface of titanium dioxide (TiO2) can be decomposed by photocatalysis under ultraviolet (UV) light. Here we describe a novel protocol employing the TiO2 photocatalysis to locally alter cell affinity of the substrate surface. For this experiment, a thin TiO2 film was sputter-coated on a glass coverslip, and the TiO2 surface was subsequently modified with an organosilane monolayer derived from octadecyltrichlorosilane (OTS), which inhibits cell adhesion. The sample was immersed in a cell culture medium, and focused UV light was irradiated to an octagonal region. When a neuronal cell line PC12 cells were plated on the sample, cells adhered only on the UV-irradiated area. We further show that this surface modification can also be performed in situ, i.e., even when cells are growing on the substrate. Proper modification of the surface required an extracellular matrix protein collagen to be present in the medium at the time of UV irradiation. The technique presented here can potentially be employed in patterning multiple cell types for constructing coculture systems or to arbitrarily manipulate cells under culture.

Photopatterning Proteins and Cells in Aqueous Environment Using TiO2 Photocatalysis

We describe a protocol for modifying cell affinity of a scaffold surface in aqueous environment. The method takes advantage of titanium dioxide photocatalysis to decompose organic film in the photo-irradiated region. We show that it can be used to create microdomains of scaffolding proteins, both ex situ and in situ.

Organic contaminants adsorbed on the surface of titanium dioxide (TiO2) can be decomposed by photocatalysis under ultraviolet (UV) light. Here we describe ...

Bioengineering

A Facile Synthetic Method to Obtain Bismuth Oxyiodide Microspheres Highly Functional for the Photocatalytic Processes of Water Depuration

Bismuth oxyhalide (BiOI) is a promising material for sunlight-driven-environmental photocatalysis. Given that the physical structure of this kind of materials is highly related to its photocatalytic performance, it is necessary to standardize the synthetic methods in order to obtain the most functional architectures and, thus, the highest photocatalytic efficiency. Here, we report a reliable route to obtain BiOI microspheres via the solvothermal process, using Bi(NO3)3 and potassium iodide (KI) as precursors, and ethylene glycol as a template. The synthesis is standardized in a 150 mL autoclave, at 126 &#176;C for 18 h. This results in 2-3 &#181;m-sized mesoporous microspheres, with a relevant specific surface area (61.3 m2/g). Shortening the reaction times in the synthesis results in amorphous structures, while higher temperatures lead to a slight increase in the porosity of the microspheres, with no effect in the photocatalytic performance. The materials are photo-active under UV-A/visible light irradiation for the degradation of the antibiotic ciprofloxacin in water. This method has demonstrated to be effective in interlaboratory tests, obtaining similar BiOI microspheres in Mexican and Chilean research groups.

This article describes a synthetic method to obtain bismuth oxyiodide microspheres, which are highly functional to perform the photocatalytic removal of organic pollutants, such as ciprofloxacin, in water under UV-A/visible light irradiation.

Bismuth oxyhalide (BiOI) is a promising material for sunlight-driven-environmental photocatalysis. Given that the physical structure of this kind of ...

Rendering SiO2/Si Surfaces Omniphobic by Carving Gas-Entrapping Microtextures Comprising Reentrant and Doubly Reentrant Cavities or Pillars

We present microfabrication protocols for rendering intrinsically wetting materials repellent to liquids (omniphobic) by creating gas-entrapping microtextures (GEMs) on them comprising cavities and pillars with reentrant and doubly reentrant features. Specifically, we use SiO2/Si as the model system and share protocols for two-dimensional (2D) designing, photolithography, isotropic/anisotropic etching techniques, thermal oxide growth, piranha cleaning, and storage towards achieving those microtextures. Even though the conventional wisdom indicates that roughening intrinsically wetting surfaces (&#952;o &#60; 90&#176;) renders them even more wetting (&#952;r &#60; &#952;o &#60; 90&#176;), GEMs demonstrate liquid repellence despite the intrinsic wettability of the substrate. For instance, despite the intrinsic wettability of silica &#952;o &#8776; 40&#176; for the water/air system, and &#952;o &#8776; 20&#176; for the hexadecane/air system, GEMs comprising cavities entrap air robustly on immersion in those liquids, and the apparent contact angles for the droplets are &#952;r &#62; 90&#176;. The reentrant and doubly reentrant features in the GEMs stabilize the intruding liquid meniscus thereby trapping the liquid-solid-vapor system in metastable air-filled states (Cassie states) and delaying wetting transitions to the thermodynamically-stable fully-filled state (Wenzel state) by, for instance, hours to months. Similarly, SiO2/Si surfaces with arrays of reentrant and doubly reentrant micropillars demonstrate extremely high contact angles (&#952;r &#8776; 150&#176;&#8211;160&#176;) and low contact angle hysteresis for the probe liquids, thus characterized as superomniphobic. However, on immersion in the same liquids, those surfaces dramatically lose their superomniphobicity and get fully-filled within &#60;1 s. To address this challenge, we present protocols for hybrid designs that comprise arrays of doubly reentrant pillars surrounded by walls with doubly reentrant profiles. Indeed, hybrid microtextures entrap air on immersion in the probe liquids. To summarize, the protocols described here should enable the investigation of GEMs in the context of achieving omniphobicity without chemical coatings, such as perfluorocarbons, which might unlock the scope of inexpensive common materials for applications as omniphobic materials. Silica microtextures could also serve as templates for soft materials.

Rendering SiO2/Si Surfaces Omniphobic by Carving Gas-Entrapping Microtextures Comprising Reentrant and Doubly Reentrant Cavities or Pillars

This work presents microfabrication protocols for achieving cavities and pillars with reentrant and doubly reentrant profiles on SiO2/Si wafers using photolithography and dry etching. Resulting microtextured surfaces demonstrate remarkable liquid repellence, characterized by robust long-term entrapment of air under wetting liquids, despite the intrinsic wettability of silica.

We present microfabrication protocols for rendering intrinsically wetting materials repellent to liquids (omniphobic) by creating gas-entrapping ...

Microhoneycomb Monoliths Prepared by the Unidirectional Freeze-drying of Cellulose Nanofiber Based Sols: Method and Extensions

Monolithic honeycomb structures have been attractive to multidisciplinary fields due to their high strength-to-weight ratio. Particularly, microhoneycomb monoliths (MHMs) with micrometer-scale channels are expected as efficient platforms for reactions and separations because of their large surface areas. Up to now, MHMs have been prepared by a unidirectional freeze-drying (UDF) method only from very limited precursors. Herein, we report a protocol from which a series of MHMs consisting of different components can be obtained. Recently, we found that cellulose nanofibers function as a distinct structure-directing agent towards the formation of MHMs through the UDF process. By mixing the cellulose nanofibers with water soluble substances which do not yield MHMs, a variety of composite MHMs can be prepared. This significantly enriches the chemical constitution of MHMs towards versatile applications.

Here, we present a general protocol to prepare a variety of microhoneycomb monoliths (MHMs) in which fluid can pass through with an extremely low pressure drop. MHMs obtained are expected to be used as filters, catalyst supports, flow-type electrodes, sensors and scaffolds for biomaterials.

Monolithic honeycomb structures have been attractive to multidisciplinary fields due to their high strength-to-weight ratio. Particularly, microhoneycomb ...

TiO₂-coated Hollow Glass Microspheres with Superhydrophobic and High IR-reflective Properties Synthesized by a Soft-chemistry Method

Podsumowanie

Przeglądaj więcej filmów

Rozdziały w tym wideo