A Facile and Eco-friendly Route to Fabricate Poly(Lactic Acid) Scaffolds with Graded Pore Size
Please note that all translations are automatically generated. Click here for the English version.
8.6K Views
•
13:46 min
•
October 17th, 2016
DOI :
October 17th, 2016
•Rozdziały w tym wideo
0:00
Title
1:43
Sodium Chloride Grinding and Sieving
2:30
Preliminary Mixing of the Materials
3:36
Compression Molding I (Monolayers)
4:56
Compression Molding II (Three-layers)
5:59
Leaching and Drying
6:27
Porosity Evaluation
7:00
Broken Scaffold in Liquid Nitrogen
7:14
Fixing Scaffold on Aluminum Stubs
7:25
Compressive Tests
7:44
Tensile Tests
7:56
Results: SEM Analysis
11:34
Results: Comprehensive Tests
12:09
Results: Tensile Tests
12:38
Conclusion
Powiązane Filmy
08:35
Elastomeric PGS Scaffolds in Arterial Tissue Engineering
15.5K Views
15:52
Postproduction Processing of Electrospun Fibres for Tissue Engineering
18.1K Views
12:19
Multi-Scale Modification of Metallic Implants With Pore Gradients, Polyelectrolytes and Their Indirect Monitoring In vivo
10.8K Views
09:37
Fabrication of a Bioactive, PCL-based "Self-fitting" Shape Memory Polymer Scaffold
12.5K Views
11:13
Composite Scaffolds of Interfacial Polyelectrolyte Fibers for Temporally Controlled Release of Biomolecules
8.3K Views
09:56
Fabrication of Mechanically Tunable and Bioactive Metal Scaffolds for Biomedical Applications
10.6K Views
10:18
Fabrication of Inverted Colloidal Crystal Poly(ethylene glycol) Scaffold: A Three-dimensional Cell Culture Platform for Liver Tissue Engineering
9.8K Views
06:36
3D Printed Porous Cellulose Nanocomposite Hydrogel Scaffolds
9.4K Views
05:52
Core/shell Printing Scaffolds For Tissue Engineering Of Tubular Structures
9.3K Views
Controlling Electrospun Polymer Morphology for Tissue Engineering Demonstrated Using hepG2 Cell Line
2.0K Views
Copyright © 2025 MyJoVE Corporation. Wszelkie prawa zastrzeżone